Abstract:In this work, we successfully report the design and synthesis of rod-like CoAl2O4/halloysite hybrid pigment from zeolitic imidazolate framework-67 (ZIF-67, a Co-based MOF) and tubular halloysite via a facile two-step route for the first time. The as-prepared nanostructures were thoroughly characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared reflection (FTIR Spectroscopy), thermogravimetric and differential scanning calorimetry (TG-DSC), X-ray photoelectron spectrometer (XPS), ultraviolet–visible spectrometry (UV–vis) and CIE L* a* b* colorimetric method. XRD patterns indicated that the presence of CoAl2O4 spinel was observed at various temperatures ranging from 800 to 1100 °C. The SEM and TEM images showed that the nano-pigment has a rod-like hybrid structure composed of nano CoAl2O4 particles and SiO2. The color performance of the fabricated pigments was evaluated and given suitable color coordinates (L* = 44.72, a* = −14.40, b* = −37.83) and (L* = 42.57, a* = −7.68, b* = −41.14) at the calcination temperature of 1100 °C for 2 h and 3 h, respectively. The mechanism study indicated that these composites were formed by Co3O4 derived of ZIF-67 as highly active cobalt source and Al2O3 decomposed from halloysite substrate as aluminum source. In addition, the corrosion resistance test showed that the CoAl2O4 composites retain crystalline stability, almost no color deviation in CIE chromatic system even after 1 M HCl leaching. Furthermore, the CoAl2O4/halloysite exhibited excellent thermal and suspension stability, which indicated it could be a promising candidate for ceramic glazes and water-borne coatings. These findings provide insight into a new strategy for the synthesis of clay mineral-based ceramic pigment.

Fabrication of Cobalt Aluminate Nanopigments by Coprecipitation Method in Threonine Waterborne Solution

Effective Synthesis of Green Nano‐sized Ceramic Pigments by Co‐doping Zn2+, Cr3+ and Sm3+ into the Cobalt‐aluminate

Synthesis and Characterization of Chromium Doped Y3Al5O12 Compound Pigment

Study of Preparation of Cobalt Aluminate by Sol-Gel Process and Electroless Plating

Novel fabrication of rod-like CoAl2O4/halloysite hybrid pigment derived from Co-MOF/nano-clay and mechanism exploration

Environmental Blue CoAl2O4 Pigment Co-Doped by Zn2+ and Mg2+: Synthesis, Structure and Optical Properties

Synthesis of an Intensive Blue Pigment with Low Cobalt Content

Aqueous Fabrication of Recyclable and Color-Adjustable Superhydrophobic Pigments Based on NiFe-Layered Double Hydroxide Nanostructures for Coating Applications

Solid‐state synthesis and characterization of cobalt blue core‐shell pigment particles

CaCO3-assisted mechanochemical synthesis of low-cost and high-chroma cobalt blue composite pigments using kaolin tailing sand for ceramic coloring

Preparation and Chromaticity Control of CoTiO3/NiTiO3 Co-Coated TiO2 Composite Pigments

Alumina Nanocoating Assisted Dispersion Stability of Permanent Violet Pigments Via Atomic Layer Deposition

Preparation of nano Fe3O4 pigment using CO32−/HCO3− as precipitant and DFT study on the formation process of its intermediate product FeOOH

Formation and Coloring Mechanism of Typical Aluminosilicate Clay Minerals for CoAl2O4 Hybrid Pigment Preparation

Cyan Ni1- x Al2+2 x/3□ x/3O4 Single-Phase Pigment Synthesis and Modification for Electrophoretic Ink Formulation

Preparation and Characterization of Nanoscale Cobalt Blue Pigment for Ceramic Inkjet Printing by Sol-Gel Self-Propagating Combustion

Synthesis and Characterization of Mixed Metal Oxide Pigments

Effect of co-precipitation synthesis parameters on gadolinium aluminate nanoparticles

Preparation, Chromatic Properties Analysis and Proportioning Optimization of Co-Cr-Fe-Based Black Pigment

Metal Ions Doped Complex Cobalt Blue Pigment Research

Preparation of nanosized CoAl2O4 powders by sol–gel and sol–gel-hydrothermal methods