Abstract:This paper proposes a two-step homogenization heat treatment to dissolve the eutectic structure and long period stacking ordered phase (LPSO) formed during solidification into the α-Mg matrix. The microstructure evolution and mechanical properties of Mg–7Gd–3Y–1Nd–2Zn–0.5Zr alloy during the two-step homogenization heat treatment have been investigated systemically. The results reveal that as-cast alloy is composed mainly of α-Mg, (Mg,Zn)3RE, eutectic phase, stacking fault, block-like LPSO phase and square-shaped compounds rich in RE. The HRTEM results suggest that the block-like long period stacking ordered phase in as-cast alloy is 14H-type rather than 18R structure, and the stacking sequences of the 14H-LPSO phase are ABABACBCBCBCAB. After the first step homogenization of 520°C for 48 h, the eutectic structure has dissolved into the matrix, whereas the 14H-LPSO phase remains in the alloy. To further dissolve the LPSO phase into matrix, the second step homogenization of 540°C for 24h was adopted. After the second-step of homogenization, the residual 14H-LPSO phase has dissolved into the matrix totally. The as-homogenized alloy is composed mainly of α-Mg and square-shaped compounds rich in RE. The tensile tests at room temperature (RT) exhibit that the ultimate tensile strength (UTS), yield strength (YS) and elongation of as-cast alloy are 172 MPa, 128MPa and 2.8%, whereas the UTS, YS and elongation of as-homogenized alloy are 253 MPa, 185 MPa and 8.4, respectively.

Solute-homogenization Model and Its Experimental Verification in Mg-Gd-based Alloys

Composition Optimization of High-Strength Mg-Gd-Y-Zr Alloys Based on the Structural Unit of Mg-Gd Solid Solution

Local atomic ordering strategy for high strength Mg alloy design by first-principle calculations

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Microstructural Characterisation of As Cast and Homogenised Mg–Gd–Nd–Zr Alloys

A study on the microstructure of as-cast and homogenized MG-GD-ND-ZR alloys

Microstructure Evolution and Mechanical Properties of Mg-7Gd-3Y-1Nd-2Zn-0.5Zr Alloy During Two-Step Homogenization Heat Treatment

Solute Pre-Precipitation and Phase Transformation in a Mg-Zn-Gd Alloy

Microstructure Evolution and Mechanical Properties of Mg-7Gd-3Y-1Nd-1Zn-0.5Zr Alloy

Effects of Rare-Earth Elements Gd and Y on the Solid Solution Strengthening of Mg Alloys

Influence of Solute Content and Cooling Rate on the Preparation of Semi-Solid Slurries for Novel Creep-Resistant Mg-Gd-Ca-Zr Alloys

Effect of Composition on Microstructural Evolution during Homogenization of 7XXX Alloys

Phase-Field Simulation on the Influence of Cooling Rate on the Solidification Microstructure of Mg-Gd-Y Ternary Magnesium Alloy

Homogenization Heat Treatment of Mg-7.68Gd-4.88Y-1.32Nd-0.63Al-0.05Zr Alloy

Effect of Y and Gd solutes on grain refinement of the as-extruded Mg-Gd(-Y)-Zn-Mn alloys

The Research of Microstructure and Mechanical Properties of Mg–7Gd–3Y–1Nd–0.5Zn–0.5Zr (wt%) Alloy

Effects of Cooling Rate and Solute Content on the Grain Refinement of Mg-Gd-Y Alloys by Aluminum

Understanding the Extrusion Microstructures in Mg Alloys Due to Solute Segregation

Atomic-scale inhomogeneous solute distribution in an ultrahigh strength nanocrystalline Al-8 Mg aluminum alloy

Solute atom mediated Hall-Petch relations for magnesium binary alloys

Effects of Isothermal Homogenization on Microstructure Evolution of Mg-7Gd-5Y-1MM-0.5Zr Alloy