Abstract:Uniform ceria nanocrystals with good crystallinity and high surface areas were prepared by a facile alcohothermal method with the addition of bases (KOH or NaOH), using Ce(III) or Ce(IV) salt as a starting material. The as-prepared nanocrystals were characterized by means of powder X-ray diffraction (PXRD), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), nitrogen adsorption, thermogravimetry and differential thermal analysis (TG-DTA), Fourier transformation infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), and ultraviolet and visible spectroscopy (UV-vis). The ceria crystals had controllable sizes from 2.6 to 6.9 nm estimated by the PXRD line broadening analysis. TEM and HRTEM micrographs showed that the as-prepared ceria nanocrystals have a relatively high degree of crystallinity and low degree of conglomeration under high base concentrations. BET specific surface areas of the as-synthesized ceria nanocrystals were very high (103-238 m(2) g(-1)). XPS spectra indicated that the cerium in the nanocrystals was predominantly tetravalent. UV-vis spectra revealed that both the direct and indirect band gap energies of the as-prepared ceria nanocrystals showed a pronounced blue-shifting due to the quantum confinement effect compared to bulk ceria. And the dielectric confinement effect on the band gap energies was also discussed. The as-prepared ceria nanocrystals supported on gamma-Al2O3 exhibited a rather lower conversion temperature (559 K) for CO oxidation to CO2 than that of bulk catalysts prepared by the coprecipitation method. Finally, a hydrolytic alcohothermal mechanism for the preparation of ceria nanocrystals was forwarded.

Controllable Synthesis and Growth Mechanism of Ceria Nanocubes by Template-Free Hydrothermal Method

Controlled Synthesis And Self-Assembly Of Ceo2 Nanocubes

Ultrafast, Continuous and Shape-Controlled Preparation of CeO2 Nanostructures: Nanorods and Nanocubes in a Microfluidic System

Facile Synthesis of Ceria Nanocrystals with Tuneable Size and Shape

Shape-selective Synthesis and Oxygen Storage Behavior of Ceria Nanopolyhedra, Nanorods, and Nanocubes.

Template-Free Synthesis Of Single-Crystalline-Like Ceo2 Hollow Nanocubes

Planar-dependent oxygen vacancy concentrations in photocatalytic CeO2 nanoparticles

Controllable synthesis of spherical cerium oxide particles

Enhanced Catalytic Activity of Ceria Nanorods from Well-Defined Reactive Crystal Planes

Ceria Nanotube Formed by Sacrificed Precursors Template Through Oswald Ripening.

Mesoporous-shelled CeO2 hollow nanospheres synthesized by a one-pot hydrothermal route and their catalytic performance

Shape-controlled synthesis of CeOHCO3 and CeO2 microstructures

Solvothermal Synthesis, Electrochemical and Photocatalytic Properties of Monodispersed CeO2 Nanocubes

Synthesis of Shape-Controlled CeO2 Nanomaterials via Microwave-Assisted Method

Green synthesis and catalytic performance of nanoscale CeO2 sheets

Preparation of Shape-Controlled Ceo2 Nanocrystals Via Microwave-Assisted Method

Mesoscale organization of nearly monodisperse flowerlike ceria microspheres.

Synthesis of Highly Uniform Ceria Nanosheets by Carbon Dioxide Carbonization and Their Growth Mechanism

Facile Alcohothermal Synthesis, Size-Dependent Ultraviolet Absorption, and Enhanced CO Conversion Activity of Ceria Nanocrystals

Spontaneous Organization of Uniform CeO2 Nanoflowers by 3D Oriented Attachment in Hot Surfactant Solutions Monitored with an in Situ Electrical Conductance Technique

Highly uniform CeO2 hierarchical microstructures: Facile synthesis and catalytic activity evaluation