SO 2 Poisoning Mechanism of the Multi-active Center Catalyst for Chlorobenzene and NO x Synergistic Degradation at Dry and Humid Environments
Guobo Li,Kai Shen,Peng Wu,Yaping Zhang,Yaqin Hu,Rui Xiao,Bing Wang,Shule Zhang
DOI: https://doi.org/10.1021/acs.est.1c03617
2021-09-15
Abstract:The performance of fresh (PdV/TiO2), sulfur poisoned (Used-S and Used-H), and regenerated (Used-RS and Used-RH) multi-active center catalysts for chlorobenzene catalytic oxidation and selective catalytic reduction (CBCO + SCR) reaction is investigated. The reaction on the catalyst surface is blocked after sulfur poisoning owing to the occupation and deposition of catalyst active centers (mainly Pd centers) by PdSO4 (and/or PdS in a dry environment) and NH4HSO4 species, especially the CBCO process. Sulfates (mainly NH4HSO4) on the sulfur poisoned catalyst surface are partially decomposed after 400 °C thermal regeneration, while the deactivation caused by the formation of PdSO4 species is irreversible. Density functional theory calculation results show that in the PdSO4 and NH4HSO4 generation paths, each step of the elementary reaction has just a small energy barrier to overcome, and the stability of the product for each elementary reaction increases gradually. Even worse, SO2 is easily combined with H2O gas molecules to form H2SO3 in a humid environment, and the energy barrier for conversion of SO32– to SO42– is just 0.041 eV. The two oxygen vacancies (VOx-1 or TiOx-1) provide adsorption sites for CBCO + SCR reaction gas molecules but do not exhibit adsorption properties for SO2, which gives a possible idea for optimization of sulfur resistance. The present work is favorable for further synergistic removal of CB/NOx by the catalyst for anti-SO2 poisoning modification and application in the manufacture industry.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.est.1c03617.Details of the Section 2 in this work; reaction condition information, general properties, gaseous reaction byproducts, and Raman analysis; HRTEM image and pyridine-IR profile (Figure S1); basic information of the Pd0.12V4/TiO2 catalyst (Table S1); CB TOF (Table S2); NO TOF (Table S3); effect of 600 ppm SO2 on CB/NO conversion and CO2/N2 selectivity (Figure S2); CB oxidation products (Table S4); gaseous compounds (Figure S3); physicochemical properties of catalysts (Table S5); SEM-EDS mapping images (Figure S4); Raman spectra (Figure S5); Ti 2p XPS profiles (Figure S6); H2-TPR profiles (Figure S7); in situ DRIFT spectra (Figure S8); corresponding species for in situ DRIFT spectra peaks (Table S6); optimized multi-active center catalyst structure (Figure S9); dehydrogenation path for H2O (Figure S10); coadsorption configurations and PDOS of SO2 with NO, NO2, O2, NH3, and H2O gas molecules (Figure S11); adsorption energy and bond information of SO2 with NO, NO2, O2, NH3, and H2O (Table S7); competitive adsorption of CB and SO2 (Figure S12); adsorption configuration and PDOS of NO, NH3, and CB on O vacancies (Figure S13); removal path and energy barrier of CB (Figure S14); configurations and PDOS for SO2 on O vacancies (Figure S15); oxidation path of PdSO4 by NO2 (Figure S16); and generation path of NH4SO4ads (Figure S17) (PDF)This article has not yet been cited by other publications.
environmental sciences,engineering, environmental