Soot Oxidation Over La0.8K0.2Mn0.95Cu0.05O3 Catalyst with SO2 at Reaction Atmosphere

Mingli Fu,Daiqi Ye,Xianghui Yue,Bichun Huang,Junliang Wu,Hong Liang

2010-01-01

Abstract:The La0.8K0.2Cu0.05Mn0.95O3 was used to oxidize model soot,and the effect of SO2 in presulfation treatment or TPO test atmosphere on catalyst performance was investigated.The catalysts were characterized with H2-TPR,FTIR and XPS.The XPS revealed that the ample OII(O-) was produced from OI(O2-) after presulfated with 0.02% SO2 at 400 ℃ for 4 h,thus promoting catalyst activity.Also 0.01%SO2 in TPO improved catalyst activity.It was probably due to that K,with excellent activity at higher temperature,could inhibit the formation and deposition of sulfate on catalyst surface,decreasing O-depletion.However,the remarkable activity loss was found after the catalyst was presulfated with 0.02% SO2 at 300 ℃ over 1 h.The O2-is nearly completely consumed and O-decreased notably,both were converted into OIII(O2-2).Probably K failed to suppress the sulfate formation and deposition at a lower temperature,thus accelerated the consumption of O2-and led to the extinction of oxygen source available,and restrained the catalyst activity.