Abstract:Carbon-fiber-reinforced polyetheretherketone (CF/PEEK) composites are widely utilized in aerospace, medical devices, and automotive industries, renowned for their superior mechanical properties and high-temperature resistance. Despite these advantages, the thermomechanical coupling behavior of CF/PEEK under dynamic loading conditions is not well understood. This study aims to explore the thermomechanical coupling effects of CF/PEEK at elevated strain rates, employing Hopkinson bar impact tests and scanning electron microscopy (SEM) for detailed characterization. Our findings indicate that an increase in temperature led to significant reductions in the yield strength, peak stress, and specific energy absorption of CF/PEEK, while fracture strain had no significant effect. For instance, at 200 °C, the yield strength, peak stress, and specific energy absorption decreased by 39%, 37%, and 38%, respectively, compared to their values at 20 °C. Furthermore, as the strain rate increased, the yield strength, peak stress, specific energy absorption, and fracture strain all exhibited strain-hardening effects. However, as the strain rate further increased, above 4000 s-1, the enhancing effect of the strain rate on the yield strength and peak stress gradually diminished. The interaction of the temperature and strain rate significantly affected the mechanical performance of CF/PEEK under high-speed impact conditions. While the strain rate generally enhanced these properties, the strain-hardening effect on the yield strength weakened as the temperature increased, and both the temperature and strain rate contributed to the increase in specific energy absorption. Microdamage mechanism analysis revealed that interface debonding and sliding between the fibers and the matrix were more pronounced under static compression than under dynamic compression, thereby diminishing the efficiency of stress transfer. Additionally, higher temperatures caused the PEEK matrix to soften and exhibit increased viscoelastic behavior, which in turn affected the material's toughness and the mechanisms of stress transfer. These insights hold substantial engineering significance, particularly for the optimization of CF/PEEK composite design and applications in extreme environments.

Influence of Temperature on the Impact Behavior of Woven-Ply Carbon Fiber Reinforced Thermoplastic Composites

Comparison of the in situ compressive behavior of carbon fibers woven ply laminates exposed to one‐sided heat flux: Thermoplastic versus thermosetting composites

Effects of high temperature and strain rate on the impact-induced inter-laminar shear behavior of plain woven CF/PEEK thermoplastic composites

Experimental investigation on low‐velocity impact performance of carbon fiber reinforced polyether ether ketone thermoplastic composite materials in room and elevated temperature

Influence of strain rate and temperature on mechanical properties of carbon woven-ply PPS thermoplastic laminates under dynamic compression

Effect of temperature on bending behavior of woven fabric-reinforced PPS-based composites

Low-velocity impact behavior of carbon woven laminates after exposure to varying temperatures

Transverse impacts‐induced deformation and damage of 3D angle‐interlock woven composites at elevated temperatures

About the influence of high temperature or fire testing conditions on the tensile behavior of carbon reinforced poly phenylene sulfide laminates

A comprehensive study of low-velocity impact behavior and damage evaluation of angle-ply thin woven GFRP composites under various temperatures

The Out-of-Plane Compression Response of Woven Thermoplastic Composites: Effects of Strain Rates and Temperature

Effects of temperature and strain rate on impact compression behaviors of three-dimensional carbon fiber/epoxy braided composites

Tensile impact behaviors and damage mechanism of woven carbon fiber-reinforced-polymer laminates considering adiabatic shear band

Elevated temperature effect on tension fatigue behavior and failure mechanism of carbon/epoxy 3D angle-interlock woven composites

An Experimental Study on the Thermomechanical Coupling Effects of Carbon-Fiber-Reinforced Polyetheretherketone under Dynamic Impact

The behaviour of thermoplastic and thermoset carbon fibre composites subjected to low-velocity and high-velocity impact

Effect of temperature and moisture composite environments on the mechanical properties and mechanisms of woven carbon fiber composites

High Strain Rate Effect Of Carbon Fiber Laminates Under Hygrothermal Environment

Internal shear damage evolution of CFRP laminates ranging from -100°C to 100°C using in-situ X-ray computed tomography

The temperature effect on the inter-laminar shear properties and failure mechanism of 3D orthogonal woven composites

Effect of Thermal Ageing on the Impact Damage Resistance and Tolerance of Carbon-Fibre-Reinforced Epoxy Laminates