Electrochemical Properties and Redox Mechanism of Na2Ni0.4Co0.6[Fe(CN)(6)] Nanocrystallites As High-Capacity Cathode for Aqueous Sodium-Ion Batteries

Wanfeng Li,Fang Zhang,Xingde Xiang,Xiucheng Zhang
DOI: https://doi.org/10.1021/acs.jpcc.7b07920
2017-01-01
Abstract:Nickel-based ferrocyanides have attracted wide interest as cathode for aqueous sodium-ion batteries in fields of sustainable energies such as wind and solar, owing to excellent cycling stability and high-rate capability. However, they suffer from low specific capacities (similar to 60 mAh g(-1)). Herein, Na2Ni0.4Co0.6[Fe(CN)(6)] nanocrystallites are reported for the first time as high-capacity cathode for aqueous sodium-ion batteries. Its electrochemical properties and redox mechanism have been understood by combining the X-ray diffraction technique, Fourier transform infrared spectroscopy, cyclic voltammetry, electrochemical impedance microscopy, and charge/discharge measurements. It is revealed that the material undergoes a reversible three-step single-phase reaction mechanism during Na extraction through sequential electro-chemical oxidation of nitrogen-coordinated Co2+ ions and carbon coordinated Fe2+ ions and achieves superior electrochemical performance with a high reversible capacity of 85 mAh g(-1) at 0.5 C, an average operating potential of 0.62 V (vs Ag/AgCl), and a high capacity retention of 90% after 100 cycles. The combination of high specific energy and good cycling performance enables the Na2Ni0.4Co0.6[Fe(CN)(6)] material exhibiting promising application for high-performance aqueous sodium-ion batteries.
What problem does this paper attempt to address?