Abstract:In recent decades, the high catalytic activity of MgAl mixed oxides (MOs) and rehydrated hydrotalcites (HTCs) has made them very promising basic catalysts for various organic reactions. The synthesis procedure as well as the mechanism of the formation of HTC structure has been well described. Despite this, little has been published on how synthetic parameters affect the physico-chemical properties, rehydration ability and performance of the hydrotalcite-derived catalysts. Here, a series of catalysts with the same molar ratio Mg/Al = 3 varied by the co-precipitation conditions (pH value, temperature, ageing duration) were synthesized and used as precursors for the preparation of the MgAl MOs and rehydrated HTCs. The set of methods (AAS, XRD, SEM, N 2 -physisorption, TGA and CO 2 -TPD) was used to establish a relation between the synthetic parameters and the physico-chemical properties of the prepared materials. Their catalytic performance was monitored in aldol condensation of furfural and acetone as a model reaction. Preparations at different pH values and temperature resulted in the formation of HTC samples with crystallite size evaluated by XRD in the range of 70–230 Å ( d 003 ). Nevertheless, the crystallite size of the resulting MOs was similar in the range of 30–36 Å ( d 003 ). The rehydration of the MOs for 5–120 min produced high-crystalline reconstructed HTC with a crystalline size in the range of 82–111 Å ( d 003 ), i.e. the crystallite size of a large-size HTC precursor was not restored. Catalytic results revealed that the crystallite size of an as-prepared HTC precursor was a crucial parameter that affected the performance of both MOs and reconstructed HTCs in the condensation reaction. Furfural conversion over MOs and short-time rehydrated (5–10 min) materials in the reaction was strongly dependent on initial size of the as-prepared HTC crystallites. In contrast, the catalytic performance of the catalysts rehydrated for 120 min, was similar: furfural conversion was above 99% in all cases. Based on these results, the effect of the physico-chemical properties of the as-prepared HTCs on the catalytic performance of both MOs and reconstructed MgAl HTCs was established. A difference in the properties of the prepared samples was explained assuming the existence of extra-framework or partially framework Al-rich species that prevented the access of reactant molecules to catalytically active sites: the larger the crystallite size of the as-prepared precursor, the higher the excess of both structural defects and non-framework Al-rich species, and the lower the furfural conversion over these catalysts. Nevertheless, long rehydration time favored the involvement of the Al-rich species in the recrystallization of HTC structure as evidenced by SEM. As a consequence, furfural conversion increased over these catalysts. These results provide a new insight into the influence of synthetic parameters on the properties of MOs and rehydrated HTCs: the crystallite size of the as-prepared precursors determines the performance of the produced catalysts in aldol condensation by affecting the rehydration ability of the derived MOs.

Effect of Hydration on the Surface Basicity and Catalytic Activity of Mg-rare Earth Mixed Oxides for Aldol Condensation

Study on Catalytic Performance and Kinetics of High Efficiency CeO2 Catalyst Prepared by Freeze Drying for the Synthesis of Dimethyl Carbonate from CO2 and Methanol

Ce/MgAl mixed oxides derived from hydrotalcite LDH precursors as highly efficient catalysts for ketonization of carboxylic acid

Catalytic Enhancement of Aldol Condensation by Oxygen Vacancy on CeO2 Catalysts

Influence of Acid-Base Properties of ZnMgAl-mixed Oxides for the Synthesis of 1-Methoxy-2-propanol

Effect of interlayer anions on the catalytic activity of Mg-Al layered double hydroxides for furfural and acetone aldol condensation reaction

Excess soluble alkalis to prepare highly efficient MgO with relative low surface oxygen content applied in DMC synthesis

PEG-assisted Synthesis of Highly Dispersed Cs/Zr-SiO2 Catalyst for Aldol Condensation of Methyl Acetate with Formaldehyde

Synergistic Catalysis by MgO Induced Acid‐Base Bifunctional Sites for Cross Condensation of HCHO and Acetaldehyde

Regulating Surface Acid-Base Balance on NaZSM-5 by Fe Modification Towards Enhanced Methanol Dehydration to Dimethyl Ether

On the influence of synthetic parameters on the properties and aldol condensation performance of the MgAl mixed oxides and rehydrated hydrotalcites

Effects of Support Modification on Nb2O5/α-Al2O3 Catalyst for Ethylene Oxide Hydration

DISPERSION OF MgO ON NaY ZEOLITE AND ITS CATALYTIC BEHAVIOR

Regulating Surface Acid-Basic Balance on Nazsm-5 by Fe3+ Solution Towards Enhanced Methanol Dehydration

Synthesis of Methyl Acrylate by Aldol Condensation of Methyl Acetate with Formaldehyde Over Al2O3-Supported Barium Catalyst

Preparation of Ce Modified Mg-Al Mixed Metal Oxides by Aqueous Reconstruction for Vapor Self-Condensation of Acetone

Preparation and Surface Hydrophilic Modification of MOR Zeolite Membrane Potentially Appling for Acetic Acid Aldol Condensation Reaction System

Hydration of ethylene oxide to ethylene glycol over SnO2-Nb2O5/MgAl2O4/alpha-Al2O3 catalyst

Geometric effect promoted hydrotalcites catalysts towards aldol condensation reaction

Synthesis, Characterization And Isopropanol Catalytic Reaction Of Mg/Al,Co/Al And Co/Mg/Al Mixed Oxides From Hydrotalcite And Hydrotalcite-Like Precursors

Hydration of Ethylene Oxide to Ethylene Glycol over SnO_2-Nb_2O_5/MgAl_2O_4/α-Al_2O_3 Catalyst