Preparation Of A Low-Phosphorous Terpolymer As A Scale, Corrosion Inhibitor, And Dispersant For Ferric Oxide
yiyi chen,yuming zhou,qingzhao yao,yunyun bu,huchuan wang,wendao wu,wei sun
DOI: https://doi.org/10.1002/app.41447
IF: 3
2015-01-01
Journal of Applied Polymer Science
Abstract:A novel low-phosphorus terpolymer, used as scale, corrosion inhibitor, and dispersant for iron oxide, was prepared through free-radical polymerization reaction of acrylic acid (AA), oxalic acid-allypolyethoxy carboxylate (APEM), and phosphorous acid (H3PO3) in water with redox system of hypophosphorous and ammonium persulfate as initiator. Structure of the synthesized AA-APEM-H3PO3 terpolymer was characterized by Fourier transform infrared spectrometer and H-1-NMR. The polymer possesses excellent scale inhibition performance for CaCO3, outstanding ability to disperse ferric oxide, and good corrosion inhibition properties. The study showed that AA-APEM-H3PO3 exhibited excellent ability to control calcium carbonate scale, with approximately 90.16% CaCO3 inhibition at a level of 8 mg/L AA-APEM-H3PO3. The data of the light transmittance showed that, compared to hydrolyzed polymaleic acid and polyepoxysuccinic acid, AA-APEM-H3PO3 had superior ability to control iron ions scaling. The light transmittance of the solution was about 24.1% in the presence of the terpolymer when the dosage was 8 mg/L. Moreover, the corrosion inhibition efficiency could reach up to 79.77% at a dosage of 30 mg/L, with ethylene diamine tetra methylene phosphonic acid just 39.62%. Scanning electronic microscopy, transmission electron microscope, and X-ray powder diffraction analysis were used to investigate the effect of AA-APEM-H3PO3 on morphology of calcium carbonate scale. The low-phosphorous terpolymer has also been proven to be effective inhibitor of calcium carbonate even at increasing solution temperature, pH, and Ca2+ concentration. The proposed inhibition mechanism suggests the surface complexation and chelation between the functional groups -P(O) (OH)(2), -COOH and Ca2+, with polyethylene glycol segments increasing its solubility in water. (C) 2014 Wiley Periodicals, Inc.