Abstract:The effect of both the Fe : Ni ratio (5 to 1 : 1) and the relative Lewis acidity of a metal oxide support on catalytic activity, selectivity and stability was investigated in the CO2 mediated oxidative dehydrogenation of ethane (CO2-ODH). To avoid effects of varying pore sizes, shapes and volumes of the supports, chromia and zirconia overlayers were coated onto a common γ-Al2O3 carrier (CrOx@Al2O3 and ZrOx@Al2O3). Separately, oxidic FexNiy alloy precursor nanoparticles were prepared using a nonaqueous surfactant-free method and deposited by sonication onto the carrier. In comparison to previous studies in the field, this synthesis technique yields closely associated iron and nickel increasing the chances for alloy formation. During reduction, a mixture of a bcc and a fcc alloy phase was formed, with the content of bcc increasing with increasing iron content as predicted by the bulk phase diagram. Upon exposure to carbon dioxide at elevated temperatures, the bcc metallic phase is selectively oxidised to an inverse spinel structure via the dissociation of CO2. When exposed to CO2-ODH conditions, the bare ZrOx@Al2O3 support shows no activity. The presence of FeNi phases increases the conversion of ethane and CO2 marginally (<2%) but forms ethylene at high selectivity (SC2H4 > 80%). The CrOx@Al2O3 support shows some initial activity (XC2H6 < 5%) at very high ethylene selectivity (SC2H4 > 90%) but deactivates with time on stream. Comparison of the ethane and carbon dioxide conversions suggests that direct dehydrogenation rather than the oxidative pathway is taking place. When FeNi particles with the highest Fe content are added, the ethane conversion behavior hardly changes, but the CO2 conversion is increased now supporting the stoichiometric CO2-ODH reaction (SC2H4 > 95%). It is therefore evident that a tandem catalyst system between a reducible oxide carrier and the FeNi species is required. Increasing the Ni content results in an increase in activity and stability while changing the dominant reaction pathway to a combination of dry reforming, CO2-ODH and possibly the reverse Boudouard reaction, with the latter countering catalyst deactivation through carbon deposition.

Tuning Ni-catalyzed CO2 hydrogenation selectivity via Ni-ceria support interactions and Ni-Fe bimetallic formation

Effect of Oxide Support on Catalytic Performance of FeNi‐based Catalysts for CO2‐assisted Oxidative Dehydrogenation of Ethane

Tuning CO2 Hydrogenation Selectivity Via Metal-Oxide Interfacial Sites

CO2 methanation over Ni nanoparticles inversely loaded with CeO2 and Cr2O3: Catalytic functions of metal oxide/Ni interfaces

Tuning the CO2 Hydrogenation Activity Via Regulating the Strong Metal–Support Interactions of the Ni/Sm2O3 Catalyst

Support effect on Ni-based mono- and bimetallic catalysts in CO2 hydrogenation

Correlating C═C, C═O, and C═N Hydrogenation Activity with Hydrogen Binding Energies on Ni–Fe Bimetallic Catalysts

Atomically Dispersed Zn‐Stabilized Niδ+ Enabling Tunable Selectivity for CO2 Hydrogenation

Elucidating the structure-activity relationship of the bimetallic Ni-Cu catalysts for CO 2 hydrogenation

Enhanced CH 4 Selectivity in CO 2 Hydrogenation on Bimetallic Pt–Ni Catalysts with Pt Nanoparticles Modified by Isolated Ni Atoms

Tunable trimetallic TM-NiFe catalysts for enhancing the products selectivity of CO 2 electroreduction

Atomically Dispersed Zn‐Stabilized Ni δ+ Enabling Tunable Selectivity for CO 2 Hydrogenation

Niobium Modification of CeO2 Tuning Electron Density of Nickel-Ceria Interfacial Sites for Enhanced CO2 Methanation

Tuning the Selectivity of Catalytic Carbon Dioxide Hydrogenation over Iridium/Cerium Oxide Catalysts with a Strong Metal-Support Interaction

Ceria-supported Ni catalyst with high catalytic activity, selectivity and stability for CO 2 conversion to CH 4 by hydrogenation reaction investigated by X-ray absorption spectroscopy

Nanostructure of nickel-promoted indium oxide catalysts drives selectivity in CO2 hydrogenation

Supported FexNiy catalysts for the co-activation of CO2 and small alkanes

Ni 12 P 5 Confined in Mesoporous SiO 2 with Near-Unity CO Selectivity and Enhanced Catalytic Activity for CO 2 Hydrogenation

Enhanced Ni–Ce Interactions to Enable Efficient Low-Temperature Catalytic CO2 Methanation

CO2 methanation on Ni-Ce0.8M0.2O2 (M=Zr, Sn or Ti) catalyst: Suppression of CO via formation of bridging carbonyls on nickel

Synthesis of Mesoporous Silica-Supported NiCo Bimetallic Nanocatalysts and Their Enhanced Catalytic Hydrogenation Performance