Abstract:A series of 20 mol% Er 3+ , x mol% Pr 3+ : Y 2.4-3x Sc 2 Ga 3 O 12 (Er 3+ , Pr 3+ : YSGG) single-crystal fibers (SCFs) were successfully grown by micro-pulling-down (μ-PD) method. Er 3+ , Pr 3+ : YSGG SCFs with varying concentrations of Pr 3+ dopant exhibit consistent retention of the identical cubic structural space group. Under 980 nm laser diode (LD) pumping, Er 3+ , Pr 3+ : YSGG exhibits two emission bands centered at 1.6 and 2.7 μm, respectively. The incorporation of Pr 3+ ions in Er 3+ , Pr 3+ : YSGG SCF materials has a negative impact on the emission peak intensity at 1.6 μm within a specific range of doping concentration, while it can relatively enhance the emission peak intensity at 2.7 μm. The lifetime of Er 3+ ions at 4 I 13/2 is showing a significant decrease trend with increasing Pr 3+ ions doping concentration. The results presented above indicate that the incorporation of Pr 3+ ions increase the likelihood of particle number inversion, improving laser operation and demonstrating the desensitizing influence of Pr 3+ ions. Quantitative analysis of the gain cross-section reveals a particle number inversion rate of 52.73% at approximately 2.7 μm. These findings provide valuable insights for developing applications aiming to achieve efficient and precise emission at 2.7 μm using Erbium–Praseodymium co-doped yttrium scandium gallium garnet single crystal fibers.

Influence Of Cr3+ Concentration On The Spectroscopy And Laser Performance Of Cr,Er:Ysgg Crystal

Effect of Er3+ concentration on spectral characteristic and 2.79 μm laser performance of Er:YSGG crystal

Pr3+ Concentration Effect on Spectroscopic Property and 3 Μm Laser Performance of Er:YAP Crystal

The influence of Pr3+ions on the emission characteristics of Er3+-doped YSGG single crystal fibers in the 1-3 m wavelength range

Improvement of Single Pulse Energy and Laser Efficiency by Co-Doping Cr3+ Ions into the Er:YAG Crystal

Absorption Spectra and Crystal-Field Modeling of Er3+ Doped in Y3sc2ga3o12 Crystal

The influence of Pr 3+ ions on the emission characteristics of Er 3+ -doped YSGG single crystal fibers in the 1–3 μm wavelength range

Influence of Cr3+ Doping on the Spectroscopies and Laser Performance of Cr,Nd:YAG Crystal Operated at 1.06 Μm

Growth, spectroscopy, and laser performance of a 2.79 μm Cr,Er,Pr:GYSGG radiation-resistant crystal.

High efficient and broadband ∼3.5 μm emission of Er3+:YAG crystal

Role of Er3+ Concentration in Spectroscopic and Laser Performance of CaYAlO4 Crystal

The influence of Pr3+ ions on the emission characteristics of Er3+-doped YSGG single crystal fibers in the 1–3 μm wavelength range

Growth, spectroscopy and high-power laser operation of Er:YAP crystal with different Er<SUP>3+</SUP> concentrations

Thermal analysis and laser performance of a GYSGG/Cr,Er,Pr:GYSGG composite laser crystal operated at 2.79 μm.

Luminescence And Thermal Properties Of Er:Gsgg And Yb,Er:Gsgg Laser Crystals

Growth and spectroscopic investigations of the 1.5 at.% Er:GSGG laser crystal

Structure, Spectroscopy and Laser Performance of an Er:YGGAG Crystal.

Growth, Spectroscopy, and Laser Performance of a 2.79 Μm Er: YSGG Single Crystal Fibers.

2.79 μm Cr,Er:YSGG laser with a high energy realized by thermal bonding and concave end-face

Spectroscopic investigations of highly doped Er<sup>3+</sup> : GGG and Er<sup>3+</sup>/Pr<sup>3+</sup> : GGG crystals

The Effects of Er3+ Ion Concentration on 2.0-Μm Emission Performance in Ho3+/Tm3+ Co-Doped Na5Y9F32 Single Crystal under 800-Nm Excitation*