Abstract:In current study, we demonstrate a strategy for improving the catalytic performance of gold (Au) for carbon dioxide reduction reaction (CO 2 RR), specifically enhancing selectivity for CO over hydrogen evolution reaction (HER) and increasing low-level CO 2 capture efficiency. This involved controlling nanostructures without any further modification. Au nanostructures having four different morphologies (i.e., degree of roughness) were fabricated via electrodeposition at varied deposition potential, resulting in different intrinsic surface hydrophobicity and exposure of high-index planes depending on the actual morphology. The roughest Au, with its combination of the most hydrophobic feature and abundant high-index planes, generated greater partial current density ( j CO ) and faradaic efficiency for CO ( FE CO ) than the other Au deposits within a tested potential region: The roughest Au showed 6-fold higher FE CO (95.8 %) and 327-fold higher j CO (normalized to electrode geometric surface area) at −0.75 V RHE compared to the smoothest Au. Moreover, the roughest Au exhibited excellent CO 2 capture ability even at low CO 2 concentration, confirmed with scanning electrochemical microscopy. These improvement at hierarchical Au for CO 2 RR could be ascribed to two factors. Firstly, the morphology-driven hydrophobicity provides an optimal gas–liquid-solid triple-phase interfaces, increasing the local CO 2 concentration near the Au catalyst surface due to its superb CO 2 capture ability. Secondly, the abundant high-index planes serve as stable active sites for CO 2 RR, expediting the reaction rates. Remarkably, Au with the highest hydrophobicity and enriched high-index planes, even without any chemical modification, showed excellent CO 2 RR catalytic performance comparable to or even better than the other previously reported Au-based catalysts.

Selective Electrochemical CO2 Reduction over Highly Porous Gold Films

Unraveling the Simultaneous Enhancement of Selectivity and Durability on Single-Crystalline Gold Particles for Electrochemical CO2 Reduction

Elucidating Mass Transport within Nanoporous Au for CO2 Electroreduction

Atomic Origins of High Electrochemical CO2 Reduction Efficiency on Nanoporous Gold.

Engineering hydrophobicity and high-index planes of gold nanostructures for highly selective electrochemical CO 2 reduction to CO and efficient CO 2 capture

Efficiency and selectivity of CO2 reduction to CO on gold gas diffusion electrodes in acidic media

Monodisperse Au Nanoparticles for Selective Electrocatalytic Reduction of Co2 to Co

Easily constructed porous silver films for efficient catalytic CO2 reduction and Zn-CO2 batteries

Selective and stable CO 2 electroreduction at high rates via control of local H 2 O/CO 2 ratio

Electrochemical Fabrication and Reactivation of Nanoporous Gold with Abundant Surface Steps for CO 2 Reduction

pH dependence of CO2 electroreduction selectivity over size-selected Au nanoparticles

Atomic origins of high electrochemical CO<sub>2</sub>reduction efficiency on nanoporous gold

Core–shell Nanoporous AuCu3@Au Monolithic Electrode for Efficient Electrochemical CO2 Reduction

Probing the Catalytically Active Region in a Nanoporous Gold Gas Diffusion Electrode for Highly Selective Carbon Dioxide Reduction

Ampere-level CO2 electroreduction with single-pass conversion exceeding 85% in acid over silver penetration electrodes

A Selective and Efficient Electrocatalyst for Carbon Dioxide Reduction

Efficient CO2 Electroreduction over Silver Hollow Fiber Electrode

Double layer charging driven carbon dioxide adsorption limits the rate of electrochemical carbon dioxide reduction on Gold

Amorphous Copper‐modified gold interface promotes selective CO2 electroreduction to CO

Selective and Scalable CO2 Electrolysis Enabled by Conductive Zinc Ion-Implanted Zeolite-Supported Cadmium Oxide Nanoclusters

Electronic and Geometric Structure Engineering of Bicontinuous Porous Ag–Cu Nanoarchitectures for Realizing Selectivity-Tunable Electrochemical CO2 Reduction