Effect of Thermal Oxidation on Microstructure and Corrosion Behavior of the PVD Hf‐Coated Mg Alloy

Dongfang Zhang,Zhengbing Qi,Binbin Wei,Zhoucheng Wang

DOI: https://doi.org/10.1002/adem.201700556

IF: 3.6

2017-01-01

Advanced Engineering Materials

Abstract:Hafnium coatings are fabricated on magnesium alloys by magnetron sputtering and are further submitted to the thermal oxidation treatment at temperature of 200, 300, and 400 °C. The thin hafnium oxide film and new grain boundaries are observed on the hafnium coatings during the appropriate treatment temperature (300 °C). These changes in microstructure result in surface densification, oxidation, and low porosity of the treated coating that significantly decrease its susceptibility to corrosion. Consequently, the thermal oxidation treatment hafnium coating exhibits a more positive corrosion potential, lower corrosion current density, and higher polarization resistance than that of the as‐deposited coating using an electrochemical system. Moreover, the enhanced adhesion of the treated coating produced by applying an appropriate treatment temperature facilitates an efficient long‐term protection of magnesium alloy.