Robust and Stable Intercalated Graphene Encapsulation of Tin Nanorods for Enhanced Cycle and Capacity Performance for Lithium Storage
Chao Wang,Jing Ju,Yanquan Yang,Yufeng Tang,Hui Bi,Fuhui Liao,Jianhua Lin,Zujin Shi,Fuqiang Huang,Ray P. S. Han
DOI: https://doi.org/10.1039/c3ra44109a
IF: 4.036
2013-01-01
RSC Advances
Abstract:Anode materials (Si, Ge, Sn, etc.) in lithium-ion batteries suffer from a remarkable loss of capacity during the charge-discharge cycle, and various carbon-based additions have been widely added to address this issue. In this work, we report on a simple, one-step approach for an intercalated graphene encapsulation of tin nanorods fabricated via the arc-discharge method. Our method is fast, robust, straight-forward and completely catalyst-free. The result is a Sn@G nanocomposite comprising of a single-crystalline Sn nanorod core tightly bonded to a highly-crystalline graphene shell. The as-synthesized Sn@G exhibits superior cycling and rate performance compared to Sn@C nanocomposite: a reversible specific capacity of 846 mA h g(-1) after 100 cycles at the current density of 200 mA g(-1) and a reversible rate capacity of 488 mA h g(-1) at 2 C for Sn@G, in contrast to the 130 mA h g(-1) and 48 mA h g(-1), respectively for Sn@C. Further, the Sn@G possesses excellent thermal and chemical stabilities against a 950 degrees C N-2 annealing and a 12 h etching in hydrochloric acid, respectively, and has a high mechanical strength as evident by the intercalated core-shell structure maintaining its shape intact in resisting the volume expansion during the 950 degrees C annealing. These encouraging results indicate that an in situ graphene encapsulated tin rods nanocomposite constitutes a highly feasible candidate for use as an anode material.