Abstract:S-doped Na2Ti6O13@TiO2 (S-TTO) core-shell nanorods, with exposed anatase TiO2 {101} facets, were synthesized by a facile calcination method. It was found that the addition of thiourea as the sulfur precursor was beneficial for the formation of anatase TiO2 with a better crystallinity and the doped sulfur atoms favorably stabilized the anatase structure. The substitution of Ti(4+) by S(6+) in the lattice of S-TTO gave rise to the visible light response and increased the amount of active groups typically as a hydroxyl radical adsorbed onto the catalyst surface. With the formation of the Ti-O-S bond, partial electrons could be transferred from S to O atoms. The electron-deficient S atoms might capture e(-) and thus inhibit the recombination of photogenerated electron-hole pairs. Meanwhile, a closely contacted interface was formed between Na2Ti6O13 and anatase TiO2, resulting in a nanoscale heterojunction structure to speed up the separation rate of photogenerated charge carriers. The exposed anatase {101} facets could act as possible reservoirs of the photogenerated electrons, yielding a highly reactive surface for the reduction of O2 to O2˙(-) and thus the decrease of recombination probability of electron-hole pairs. In addition, the anisotropically shaped titanate nanorods provided a pathway for the quick transport of charge carriers throughout the longitudinal direction. The combined effects of S doping, nano-heterojunction formation and morphology engineering led to an obviously enhanced photocatalytic performance for the degradation of methylene blue (MB) solution under visible light irradiation. The corresponding photocatalytic mechanism was investigated and discussed in detail. The present work may provide an insight into the fabrication of delicate composite photocatalysts with excellent performance.

Na2Ti6O13@TiO2 Core-Shell Nanorods with Controllable Mesoporous Shells and Their Enhanced Photocatalytic Performance

S-doped Na2Ti6O13@TiO2 Core-Shell Nanorods with Enhanced Visible Light Photocatalytic Performance.

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Electrodeposited Cu2O on the {101} Facets of TiO2 Nanosheet Arrays and Their Enhanced Photoelectrochemical Performance

N-doped Na2Ti6O13@TiO2 Core–shell Nanobelts with Exposed {1 0 1} Anatase Facets and Enhanced Visible Light Photocatalytic Performance

Balsam-Pear-Like Rutile/Anatase Core/Shell Titania Nanorod Arrays For Photoelectrochemical Water Splitting

Preparation of SiO2@Au@TiO2 Core–shell Nanostructures and Their Photocatalytic Activities under Visible Light Irradiation

Facile Synthesis of CdS@TiO2 Core–shell Nanorods with Controllable Shell Thickness and Enhanced Photocatalytic Activity under Visible Light Irradiation

Single-crystal TiO 2 /srtio 3 Core–shell Heterostructured Nanowire Arrays for Enhanced Photoelectrochemical Performance

Yolk-Shell Tio2-Nrs@Sio2 with Enhanced Photocatalytic Hydrogen Production

Facile Synthesis of Ni-doped TiO2ultrathin Nanobelt Arrays with Enhanced Photocatalytic Performance

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Preparation of In2O3@TiO2 core-shell spherical nanocomposites with the enhanced photocatalytic activity under solar light irradiation

Large-Scale Preparation Of Ordered Titania Nanorods With Enhanced Photocatalytic Activity

Single-crystal Heterostructured PbTiO3/CdS Nanorods with Enhanced Visible-Light-driven Photocatalytic Performance

A Novel Etching and Reconstruction Route to Ultrathin Porous TiO2 Hollow Spheres for Enhanced Photocatalytic Hydrogen Evolution

Preparation and Characterization of SiO<SUB>2</SUB>/TiO<SUB>2</SUB>-Pt Core/Shell Nanostructures and Evaluation of Their Photocatalytic Activity

Branched core-shell a-TiO2@N-TiO2 nanospheres with gradient-doped N for highly efficient photocatalytic applications

Novel Tio2-Pt@Sio2 Nanocomposites With High Photocatalytic Activity

Novel TiO₂-Pt@SiO₂ nanocomposites with high photocatalytic activity

TiO2@g-C3N4 core/shell spheres with uniform mesoporous structures for high performance visible-light photocatalytic application