Abstract:Ozone pollution has become one of the most concerned environmental issue. Developing low-cost and efficient catalysts is a promising alternative for ozone decomposition. This work presents a creative strategy that using alpha-Fe2O3-supported Co3O4 nanoparticles for constructing interfacial oxygen vacancies (Vo) to remove ozone. The efficiency of Co3O4/alpha-Fe2O3 was superior to that of pure alpha-Fe2O3 by nearly two times for 200-ppm ozone removal after 6-h reaction at 25 degrees C, which is ascribed to the highly active interfacial Vo. X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy suggest that the Fe3+-Vo-Co2+ was formed when Co3O4 was loaded in alpha-Fe2O3. Furthermore, the density functional theory (DFT) calculations reveal the desorption and electron transfer ability of intermediate peroxide (O-2(2-)) on Fe3+-Vo-Co2+ are higher than the Vo from other regions. In situ diffuse reflectance Fourier transform (DRIFT) spectroscopy also demonstrate the higher conversion rate of O-2(2-) on Co3O4/alpha-Fe2O3. Base on the intermediates detected, we propose a recycle mechanism of interfacial Vo for ozone removal: O-2(2-) is quickly converted to O-2(2-) and transformed into O-2 on interfacial Vo. Moreover, O-2-temperature programmed desorption (TPD), H-2-temperature-programmed reduction (TPR), and electrochemical impedance spectroscopy (EIS) reveal that the oxygen mobility, reducibility, and conductivity of Co3O4/alpha-Fe2O3 are greatly superior to those of alpha-Fe2O3, which is contributed to the conversion of O-2(2-). Consequently, our proposed strategy effectively enhances the activity and stability of the bimetallic transition oxides for ozone decomposition.

Facile synthesis of Fe-modified manganese oxide with high content of oxygen vacancies for efficient airborne ozone destruction

Enhanced catalytic oxidation of toluene over manganese-based multi-metal oxides synthesized by ozone driving redox reaction

Facile Synthesis of Amorphous MnOx Catalysts for Efficient Ozone Elimination in Domestic Refrigerators

Ce–Fe–Mn Ternary Mixed-Oxide Catalysts for Catalytic Decomposition of Ozone at Ambient Temperatures

Highly efficient removal of ozone by amorphous manganese oxides synthesized with a simple hydrothermal method

Efficient ozone decomposition in high humidity environments using novel iron-doped OMS-2-loaded activated carbon material

Facile Synthesis Of Amorphous Mesoporous Manganese Oxides For Efficient Catalytic Decomposition Of Ozone

Highly Efficient Ozone Decomposition Against Harsh Environments over Long-Term Stable Amorphous MnOx Catalysts

Generation of Abundant Oxygen Vacancies in Fe Doped Δ-Mno2 by a Facile Interfacial Synthesis Strategy for Highly Efficient Catalysis of VOCs Oxidation

Surface Oxygen Vacancy Induced Α-Mno2 Nanofiber for Highly Efficient Ozone Elimination

Α-Fe2o3-supported Co3O4 Nanoparticles to Construct Highly Active Interfacial Oxygen Vacancies for Ozone Decomposition.

Catalytic Decomposition of Airborne Ozone by MnCO3 and Its Mechanism

Vanadium-doped MnO2 for Efficient Room-Temperature Catalytic Decomposition of Ozone in Air

Highly Efficient Removal of Ozone on Amorphous Manganese Oxides Modified by Alkali Metals

Enhanced low-temperature NO oxidation by iron-modified MnO2 catalysts

Interface Reconfiguration of MnCO3/Mn3O4 Heterostructure Enhances the Ozone Decomposition in the Entire Humidity Range

Enhancing ozone catalytic decomposition through acid treatment of α-MnO2 for improved activity and humidity resistance

Efficient monolithic MnOx catalyst prepared by heat treatment for ozone decomposition

Facile Synthesis of Activated Carbon-Supported Porous Manganese Oxide via in situ Reduction of Permanganate for Ozone Decomposition

Ammonium-treated birnessite-type MnO2 to increase oxygen vacancies and surface acidity for stably decomposing ozone in humid condition

Exceptional Ozone Decomposition over -MnO2/AC under an Entire Humidity Environment