Interface Optimization and Mechanical Properties of Cu-Coated Carbon Fiber Cloth/Titanium Alloy Composite

Yang Zhiming,Wu Tengteng,Liu Jinxu,Zhou Lin,Li Shukui

DOI: https://doi.org/10.1016/s1875-5372(17)30114-5

2017-01-01

Rare Metal Materials and Engineering

Abstract:Using Cu-coated carbon fiber cloth (CFC) as reinforcement and Ti-6Al-4V (TC4) as matrix,the Cu-coated CFC/TC4 composite was fabricated by spark plasma sintering.The interface morphology,phase microstructure,phase distribution and mechanical properties of CFC/TC4 were characterized.Results show that carbon fibers are uniformly distributed in Cu-coated CFC/TC4.CuTi,Cu and trace TiC are distributed along the interface between fibers and matrix.The Cu-coated CFC/TC4 possesses slightly better plasticity than TC4,and the yield strength and compressive strength are obviously enhanced.The electroplated Cu plays important roles:(1) markedly decreasing the sintering temperature of Cu-coated CFC/TC4;(2) significantly improving the wettability and interfacial bonding between carbon fibers and TC4 matrix,thus increasing mechanical properties of Cu-coated CFC/TC4;(3) effectively inhibits the excessiving generation of brittle TiC compared with uncoated CFC/TC4 composite,thus maintaining good plasticity of Cu-coated CFC/TC4.