Abstract:Nano-ZSM-5 with large amount and high strength of acid sites were successfully synthesized by hydrothermal crystallization of pure-silica nucleus in NaAlO2 alkali solution. The concentration of NaAlO2 alkali solution was decreased by increasing the H2O/Al ratio from 200 to 2600, which strongly determined the acidic properties and crystal size of the obtained nano-ZSM-5. Low concentration of NaAlO2 alkali solution was found unfavorable for the incorporation of Al into the bulk of ZSM-5 crystal in crystallization process. Hence, more Al distributed at the exterior of crystals, which enhanced the accessibility of the acid sites during reaction. Large amount and high strength of acid sites were produced for nano-ZSM-5 by increasing H2O/Al ratio. When the H2O/Al ratio increased from 200 to 2600, the total amount of acid sites increased from 0.59 to 0.81 mmol g(-1), much higher than conventional value of 0.50 mmol g(-1). In addition, the acid strength increased and the ratio of Bronsted/Lewis acid sites were sharply increased from 2.3 to 4.1 when the H2O/Al ratio increased. Moreover, the size of nano-crystal was also decreased by above decreasing the concentration of the NaAlO2 alkali solution. When the H2O/Al ratio was 2600, the obtained sample possessed total acid amount of 0.81 mmol g(-1) and crystal size of 60 nm, respectively. Methanol to hydrocarbon (MTH) reaction results showed that the increased acid sites of the catalyst decreased its catalytic lifetime to some extent, but the aromatics selectivity was tunable obviously. As for the catalyst prepared with H2O/Al ratio of 2000, the aromatics selectivity of the obtained catalyst reached to 66.0%. This paper provided a method for the fabrication of small-size nano-ZSM-5 with large amount and high strength of acid sites and regulated Al distribution for MTH reaction.

Near-Graphite Coke Deposit on Nano-Hzsm-5 Aggregates for Methanol to Propylene and Butylene Reaction

Effect of Hydrothermal Treatment on Suppressing Coking of Zsm-5 Zeolite During Methanol-To-Propylene Reaction

A facile route to synthesize endurable mesopore containing ZSM-5 catalyst for methanol to propylene reaction.

Effect of the Si/Al Ratios of Nanocrystalline HZSM-5 Zeolite on the Performance in Catalytic Conversion of Ethanol to Propylene

Catalytic Study of Methanol-to-Propylene Conversion over Nano-Sized HZSM-5

Catalytic Performance and Coking Behavior of a Submicron HZSM‐5 Zeolite in Ethanol Dehydration

Catalytic Cracking of 1-Butene to Propylene by Ag Modified HZSM-5

In Situ Solid State NMR Observation of the Methanol-to-hydrocarbons (MTH) Process over Nanosized and Microsized HZSM-5 Zeolites

Multinuclear Solid-State NMR Characterization of the Coke on Mo/Hβ-Al_2O_3 Catalyst for Olefin Metathesis

Influence of framework Al distribution in HZSM-5 channels on catalytic performance in the methanol to propylene reaction

In-Situ Synthesis of Zsm-5 Zeolite from Metakaolin/Spinel and Its Catalytic Performance on Methanol Conversion

Programmable synthesis of mesoporous ZSM-5 nanocrystals as selective and stable catalysts for the methanol-to-propylene process

Direct synthesis of HZSM-5 zeolites with enhanced catalytic performance in the methanol-to-propylene reaction

Relay and Feedback Conversion Effect of Hydrocarbons between ZSM-5 Grains on Product Selectivity and Coke Formation during Methanol Aromatization

Regulation of framework Al distribution of high-silica hierarchically structured ZSM-5 zeolites by boron-modification and its effect on materials catalytic performance in methanol-to-propylene reaction

Controllable Synthesis of Nano-Zsm-5 Catalysts with Large Amount and High Strength of Acid Sites for Conversion of Methanol to Hydrocarbons

Effect of Preparation Method on the Catalytic Performance of HZSM-5 Zeolite Catalysts in the MTH Reaction

Synthesis of nano-size HZSM-5 and their performances in MTP reaction

Selective production of propylene from methanol: Mesoporosity development in high silica HZSM-5

The effects of carbonaceous species in HZSM-5 on methanol-to-olefin process

Conversion of Methanol to Propylene over a High Silica B-HZSM-5 Catalyst