Abstract:A highly selective, gas-phase benzyl alcohol-to-benzaldehyde transformation is achieved over mesoporous multi-component metal oxide K-Cu-TiO2 (prepared by AcHE process) at a surprisingly low temperature: the b.p. of benzyl alcohol, 203?degrees C. We propose that highly efficient selective oxidation over K-Cu-TiO2 occurs through an oxidative dehydrogenation mechanism based on the catalytic performance with controlled oxygen addition and the observation of surface hydride species on the catalyst surface by electron paramagnetic resonance spectroscopy and spin-trapping techniques. It was observed that the benzyl alcohol conversion increased sharply with the increase in p?O?2 and reached a maximum of 80.4?% at p?O?2/pBA=0.40.6. A further increase in the p?O?2 slightly decreased the benzyl alcohol conversion. The fact that the reaction rate was independent of the oxygen pressure after the stoichiometric p?O?2/pBA ratio (0.5) could indicate a fast reoxidation of CuI?H by molecular oxygen, which is, therefore, not the rate-controlling step. No hydride species have been detected on the catalyst that was collected from the alcohol oxidation reaction performed with added O2, suggesting that O2 acts as efficient hydrogen acceptor and accelerate the reaction by liberating free active CuI sites. Based on understanding of the reaction mechanism, in addition to the low-temperature reaction condition, stoichiometrical addition of O2 proves effective in the stabilisation of the CuI oxidation state for highly selective benzyl alcohol oxidative dehydrogenation over a wide reaction temperature range (up to 310?degrees C).

Room Temperature Selective Oxidation of Benzyl Alcohol under Base-Free Aqueous Conditions on Pt/TiO2

Green Catalytic Oxidation of Benzyl Alcohol over Pt/ZnO in Base-Free Aqueous Medium at Room Temperature

Synergistic effect between Pt0 and Bi2O3−x for efficient room-temperature alcohol oxidation under base-free aqueous conditions

Synergistic Effect Between Pt-O And Bi2o3-X For Efficient Room-Temperature Alcohol Oxidation Under Base-Free Aqueous Conditions

Highly Selective Oxidation of Benzyl Alcohol to Benzaldehyde with Hydrogen Peroxide by Biphasic Catalysis

In Situ Hydrogen Peroxide Production for Selective Oxidation of Benzyl Alcohol over a Pd@Hierarchical Titanium Silicalite Catalyst

Low‐Temperature Gas‐Phase Oxidation of Benzyl Alcohol on Mesoporous K‐Cu‐TiO2 Through Oxidative Dehydrogenation

Solvent-Free Selective Photocatalytic Oxidation of Benzyl Alcohol over Modified Tio2

Base-free aqueous-phase oxidation of non-activated alcohols with molecular oxygen on soluble Pt nanoparticles

Selective Aerobic Oxidation of Aromatic Alcohols Catalyzed by Tio(2): an Insight on the Effect of Surface Fluorination

Solvent-free oxidation of benzyl alcohol with oxygen using zeolite-supported Au and Au–Pd catalysts

Base-free selective oxidation of benzyl alcohol in water over palladium catalyst supported on titanium niobate nano sheets

Selective solvent-free oxidation of toluene to benzaldehyde over zeolite supported iron

Low-temperature, Highly Selective, Gas-Phase Oxidation of Benzyl Alcohol over Mesoporous K-Cu-TiO2 with Stable Copper(i) Oxidation State.

Au-Pd Nanoparticles Immobilized on TiO2 Nanosheet As an Active and Durable Catalyst for Solvent-Free Selective Oxidation of Benzyl Alcohol.

Oxidation of Benzyl Alcohol Compounds in the Presence of Carbon Hybrid Supported Platinum Nanoparticles (Pt@CHs) in Oxygen Atmosphere

Biosynthesized Bimetallic Au–Pd Nanoparticles Supported on TiO2 for Solvent-Free Oxidation of Benzyl Alcohol

Titanium‐Microfiber‐Supported Binary‐Oxide Nanocomposite with a Large Highly Active Interface for the Gas‐Phase Selective Oxidation of Benzyl Alcohol

One-Step Hydrothermal/Solvothermal Preparation of Pt/TiO2: An Efficient Catalyst for Biobutanol Oxidation at Room Temperature

Au@Pd/TiO2 with atomically dispersed Pd as highly active catalyst for solvent-free aerobic oxidation of benzyl alcohol