Investigation on the Preparation of Silicone-polyurethane Latex, Phase Structure and Property of the Latex Films
Min Xu,Jie Shen,Hong Zhang,Yang Hu,Ling-xiao Li,Cheng-you Kan
DOI: https://doi.org/10.11777/j.issn1000-3304.2016.16096
2016-01-01
Acta Polymerica Sinica
Abstract:Using hydroxypropyl terminated polydimethylsiloxane ( HP. PDMS ), isophorone diisocyanate and 2,2-bis( hydroxymethyl ) butyric acid as starting materials, silicone-polyurethane copolymer ( Si-PU ) latexes with particle diameter of about 50 nm were prepared via step-by-step feeding process followed by phase inversion technique in the absence of surfactant. Influences of the HP-PDMS content on the phase structure and the properties of the Si-PU latex films were investigated, and the difference between Si-PU and polyether polyurethane ( E-PU ) was emphasized. It was found that the content of PDMS in Si-PU could reach up to 65 wt%. Results of DSC analysis showed that, in comparison with the E-PU latex film, the Si-PU latex films exhibited well phase separation. Strong hydrogen bonding in Si-PU hard segments was confirmed by FTIR, which promoted the micro. phase separation in the latex films. On the contrary, strong hydrogen bonding existed in between the soft and hard segments in E-PU, which led to phase mixing and prevented the formation of phase separation structure. The Si-PU latex films were characterized by AFM tapping mode and the formation of sea. island phase separation was observed, and this kind of phase separation structure in the Si-PU latex films was rarely reported in the literature, in which the amorphous PDMS. enriched domains constituted the dispersed phases. With the increase in HP. PDMS content, the degree of phase separation in the Si-PU latex films increased as well, which led to the decrease of elastic modulus from 400.0 MPa to 32.2 MPa with an increase in elongation at break and in the flexibility. The initial decomposition temperature of the Si-PU latex films was at about 244 degrees C, which was 18 degrees C lower than that of the E-PU latex film due to the low degree of hydrogen bonding between the soft and the hard segments, whereas the thermal stability of Si-PU at high temperature zone was much better than E-PU. Compare to the E-PU latex film, a low water adsorption rate under 11% and a high contact angle above 94 degrees indicated excellent water resistance of the Si-PU latex films.