Structural Evolution of Hard-Elastic Isotactic Polypropylene Film During Uniaxial Tensile Deformation: the Effect of Temperature
Yuanfei Lin,Xueyu Li,Lingpu Meng,Xiaowei Chen,Fei Lv,Qanlei Zhang,Rui Zhang,Liangbin Li
DOI: https://doi.org/10.1021/acs.macromol.8b00255
IF: 5.5
2018-01-01
Macromolecules
Abstract:The effects of temperature on the nonlinear mechanical behaviors of hard-elastic isotactic polypropylene films are systematically studied with in-situ ultrafast synchrotron radiation small- and wide-angle X-ray scattering techniques (SAXS/WAXS) during uniaxial tensile deformation at temperatures from 30 to 160 degrees C. Based on the mechanical behaviors and structural evolutions in strain temperature two-dimensional space, three temperature regions (I, II, and III) are clearly defined with the alpha relaxation temperature (T-alpha approximate to 80 degrees C) and the onset of melting temperature (T-onset approximate to 135 degrees C) as boundaries, where different mechanisms dominate the nonlinear deformations after yield. In region I, microstrain in lamellar stacks epsilon(m) obtains an accelerated increase after yield and reaches a value significantly larger than corresponding macrostrain epsilon, during which neither slipping, melting, nor cavitation occurs. We propose stress-induced microphase separation of interlamellar amorphous to be responsible to the hyperelastic behavior in region I. Above T-alpha in region II, due to reduced cohesive strength and enhanced chain mobility, the irreversible reduction of crystallinity and the formation of slender cavities suggest that crystal slipping overwhelms microphase separation and plays the major role in nonlinear deformation, during which chains in lamellar crystals are pulled out and recrystallize into nanofibrillar bridges. In region III above T-onset, melting recrystallization dictates the nonlinear deformation. A schematic roadmap for structural evolution is constructed in strain temperature space, which may guide the processing of microporous membranes for lithium battery separators as well as other high performance polymer fibers and films.