Abstract:Zn modified ZSM-5 zeolite supported Ni bifunctional catalysts were prepared by in-situ hydrothermal synthesis (Zn-Ni-ZSM-5), co-impregnation method (Zn-Ni/ZSM-5) as well as combining in-situ hydrothermal synthesis of Zn-ZSM-5 and sequential impregnation of Ni (Ni/Zn-ZSM-5) and used for the selective converting olefin to aromatics applicable for FCC gasoline hydro-upgrading. The Lewis (L) acid sites generated by ZnOH+ species and hydrogenation active sites from Ni0 species were varied with preparation method, in which their locations at the external surface or micropores of zeolite changed the acid properties of catalysts. Comparing to the Zn-Ni/ZSM-5 from the co-impregnation method, direct in-situ hydrothermal method could incorporate Zn and Ni species within zeolite, which makes the strong interaction between the metal species and the framework Al to form medium-strong L acids (ZnOH+/NiOH+). This leads to the decrease of ratio of Brønsted acid sites to L acid sites (B/L) from 0.40 to 0.12 and the difficulty in reducing of Ni cations to Ni0 from 57% to 30% Ni0 percent. Ni/Zn-ZSM-5 sample prepared by incorporating Zn species into micropores and sequential depositing Ni species at the external surface of zeolite possesses a low B/L ratio similar to Zn-Ni-ZSM-5 (0.20 versus 0.12) but a much higher Ni0 percent (52% versus 30%). Zn-Ni-ZSM-5 shows closer intimacy between Zn and Ni species comparing to Zn-Ni/ZSM-5 and Ni/Zn-ZSM-5. For the 1-hexene aromatization, the formed iso-alkene at acid sites was quickly saturated to iso-alkanes by the adjacent Ni0 particles over Ni-Zn-ZSM-5 catalyst in hydrogen steam. However, the location of aromatization active sites (ZnOH+, L acid sites) in micropores and hydrogenation active sites (Ni0 species) on external surface of Ni/Zn-ZSM-5 makes the tandem conversion of n-alkene → iso-alkene → aromatics, rather than the n-alkene → iso-alkene → iso-alkane. Thus, Zn-Ni-ZSM-5 with close intimacy of ZnOH+ and Ni0 particles shows a high iso-alkane selectivity (27.9% iC4 +), while Ni/Zn-ZSM-5 exhibits a high aromatics selectivity (39.6 %) in the conversion of 1-hexene in hydrogen steam. Similar results have also found in the conversion of n-heptane. Here, the control of the intimacy of Zn and Ni in ZSM-5 zeolites has been realized to be a good protocol to adjust the selective conversion of olefins/alkanes to aromatics versus iso-alkanes.

Sn and Zn Modified Hzsm-5 for One-Step Catalytic Upgrading of Glycerol to Value-Added Aromatics: Synergistic Combination of Impregnated Sn Particles, Ald Introduced Zno Film and Hzsm-5 Zeolite

Enhanced performance of glycerol to aromatics over Sn-containing HZSM-5 zeolites

Synergy Effect Between Hierarchical Structured and Sn-modified H[Sn, Al]ZSM-5 Zeolites on the Catalysts for Glycerol Aromatization

Catalytic Cracking of Fatty Acid Methyl Esters for the Production of Green Aromatics Using Zn-Modified HZSM-5 Catalysts

Shape Selectivity Conversion of Biomass Derived Glycerol to Aromatics over Hierarchical HZSM-5 Zeolites Prepared by Successive Steaming and Alkaline Leaching: Impact of Acid Properties and Pore Constraint

Efficient Conversion of Glycerol to Aromatics over Stable Nanosized X-Zf/zm-y Catalysts Using ZIF-8 As a Template

Effects Of Additives And Metals On Crystallization Of Nano-Sized Hzsm-5 Zeolite For Glycerol Aromatization

Synthesis Of Nanoscale Hzsm-5 Zeolite And Its Application In Alkylation, Dehydration Of Bio-Ethanol And Upgrading Of Fcc Gasoline

ZSM-5 Zeolite Catalyst for Reduction of Gasoline Olefins Via Aromatization

Simultaneously enhanced aromatics selectivity and catalyst lifetime in methanol aromatization over [Zn, Al]-ZSM-5 via isomorphous substitution with optimized acidic properties and pore structure

Conversion of Glycerol to Aromatics Over Hollow Hzsm-5 Based Catalyst: Effects of Metal Modification and Preparation Method

Tailoring the impact of synthetic strategies on the catalytic upgrading of crude glycerol to produce bio-based aromatics in hierarchical HZSM-5

Stable Zn@ZSM-5 catalyst via a dry gel conversion process for methanol-to-aromatics reaction

The Synergistic Effect of Hydroxylated Carbon Nanotubes and Ultrasound Treatment on Hierarchical HZSM-5 in the Selective Catalytic Upgrading of Biomass Derived Glycerol to Aromatics

A Highly Active and Stable Zn@C/HZSM-5 Catalyst Using Zn@C Derived from ZIF-8 As a Template for Conversion of Glycerol to Aromatics

Synthesis and consequence of Zn modified ZSM-5 zeolite supported Ni catalyst for catalytic aromatization of olefin/paraffin

Producing BTX Aromatics-Enriched Oil from Biomass Derived Glycerol Using Dealuminated HZSM-5 by Successive Steaming and Acid Leaching As Catalyst: Reactivity, Acidity and Product Distribution

Bifunctional Catalysts for One-Step Conversion of Syngas into Aromatics with Excellent Selectivity and Stability

Catalytic upgradation of crude glycerol to produce bio-based aromatics over hierarchical MFI zeolite: Effect of bimodal hierarchical porosity enhancement and porosity-acidity interaction

The growth mode of ZnO on HZSM-5 substrates by atomic layer deposition and its catalytic property in the synthesis of aromatics from methanol

Successive Desilication and Dealumination of HZSM-5 in Catalytic Conversion of Waste Cooking Oil to Produce Aromatics