Abstract:The fundamental degradation mechanism of Polycrystalline Diamond Compact (PDC) cutters during granite turning were investigated at various cutting forces and cutting temperature by changing the turning depths and using cooling water or not. The microstructures and compositions of the worn PDC surfaces were characterized by Scanning Electron Microscope (SEM), Energy Dispersive Spectrometer (EDS) and Raman Spectroscope. In this experiment, PDC turning granite tests under dry and wet conditions with four different cutting depths were conducted.Three different failure modes of PCD were observed. Under wet turning, when the turning depths were 0.2 mm and 0.4 mm, the main failure was the abrasion of diamond due to the cobalt at grain boundaries catalyzing sp3 to sp2 transformation. When the turning depth reaches 0.6 mm, both the graphitization on surface and the cobalt thermal expansion subsurface occurred, which result in the flaky pits on diamond surface. Under dry turning, the temperature of the PDC surface increases gradually with increasing depth of cut. Cobalt at surface and beneath undergoes significant thermal expansion and the introduced thermal stresses break the diamond to diamond (DD) bondings. In , there are two main mechanisms of PDC degradation, the inverse catalysis of cobalt and the in-situ thermal expansion of cobalt were found. For wet turning test, the PDC cutting temperature grows relatively slow, cobalt at grain boundaries on the the diamond surface is firstly abraded. At the same time, due to the thermal expansion at high temperatures cobalt could be partially squeezed out of the grain boundaries, accelerating the transformation of diamond to graphite and leading to the scratching of diamond grains by sharp granite. For dry turning test, the PDC cutting temperature dramatically increases, cobalt at grain boundaries in-situ thermal expanses and cause the huge thermal stresses, resulting in diamond transgrainular cracking and spalling out.

Polycrystalline Diamond Compact with Enhanced Thermal Stability

Research Progress of Thermal Stability for Polycrystalline Diamond

Nanoengineered Polycrystalline Diamond Composites with Advanced Wear Resistance and Thermal Stability

Nano-polycrystalline diamond formation under ultra-high pressure

Effect of pressure on sintering behavior of polycrystalline diamond

Preparation, wear resistance, and impact toughness of homoepitaxial diamond film deposited on polycrystalline diamond compact by HFCVD method

Novel high-performance polycrystalline diamond compact enhanced using vanadium additives

Temperature-mediated Structural Evolution of Vapor–phase Deposited Cyclosiloxane Polymer Thin Films for Enhanced Mechanical Properties and Thermal Conductivity

Ultrastrong catalyst-free polycrystalline diamond

Tribological behavior of PDC-cutter including cemented carbide and polycrystalline diamond composites produced by HPHT for drilling applications

Polycrystalline Diamond Cutters Sintered with Magnesium Carbonate in Cubic Anvil Press

Impact of Ce 2 O 3 on microstructure and properties of matrix-body for PDC drill bits synthesized via pressureless melt infiltration

Effect of diamond layer thickness on tool wear of polycrystalline diamond composites

Researches and Prospects of Polycrystalline Diamond Compacts

The Wear and Friction Characters of Polycrystalline Diamond under Wetting Conditions

Study on Welding Technique of PDC

The novel and facile electrolysis method for removing the cobalt binder phase from large diameter polycrystalline diamond compacts

A Study on the Microstructure of Polycrystalline Diamond Composite (PDC) for Valves

Preparation of Ti-coated diamond/WC-Co-based cemented carbide composites by microwave-evaporation titanium-plating of diamond particles and microwave hot-press sintering

An advanced investigation of polycrystalline diamond compact's degradation mechanism during granite turning

Effect of ZrB$_2$ additions on the thermal stability of polycrystalline diamond