Abstract:In this study, a series of high-performance biobased liquid crystal copolyesters derived from 6-hydroxy-2-naphthoic acid (HNA), 4, 4ʹ-Dihydroxybiphenyl (BP), biobased 2,5-furandicarboxylic acid (FDCA) and sebacic acid (SeA) were successfully designed and prepared via “one-pot” melt polycondensation method. The addition of nonlinear and rigid FDCA units broke the regularity of the molecular chain but increased the chain rigidity, thus, endowing the unique thermal behavior, which the melting temperature decreased from 163.0 to 125.3 ℃, while the glass transition temperature decreased first and then increased slightly to 75.7 ℃ as increased the FDCA units to 7.5 mol%. Furthermore, DSC and XRD results showed that a small amount (1 mol%) of FDCA units did not impair crystallization ability of the copolyesters, whereas excess of FDCA hindered the molecular chain packing. The DMA results also demonstrated that the addition of FDCA restricts the chain motion and improves the rigidity of the copolyester as reflected by the higher storage modulus. The incorporation of nonlinear FDCA units lowered the initial degradation temperature slightly, but still exhibited enough thermal stability to be melt processed as compared with its relative low melting temperatures. The copolyesters exhibited a broad temperature range of nematic liquid crystal phase as well as shear thinning and viscous melt flow behavior, which were beneficial for its melt processing. The tensile strength and modulus of the injection molded splines were in range of 82.51–103.27 MPa and 2.05–2.72 GPa, respectively, which were much higher than the common biobased copolyesters such as PLA, PCL and other FDCA-containing polyesters. The increased modulus and decreased fracture strain of the copolyesters containing FDCA units further verified the high rigidity of the molecular chain. Moreover, the in-vitro cytotoxicity and water contact angle results proved that the copolyesters have good biocompatibility. The resulted copolyesters combined with excellent melt processing ability, mechanical property and good biocompatibility have great promising applications as biomedical and biodegradable materials.

Biobased Copolyesters: Synthesis, Crystallization Behavior, Thermal and Mechanical Properties of Poly(ethylene Glycol Sebacate-Co-ethylene Glycol 2,5-Furan Dicarboxylate)

Biobased Poly(ethylene-co-hexamethylene 2,5-Furandicarboxylate) (PEHF) Copolyesters with Superior Tensile Properties

DBU-catalyzed biobased poly(ethylene 2,5-furandicarboxylate)polyester with rapid melt crystallization : synthesis, crystallization kinetics and melting behavior

Modification of Poly(ethylene 2,5-Furandicarboxylate) with Biobased 1,5-Pentanediol: Significantly Toughened Copolyesters Retaining High Tensile Strength and O2 Barrier Property

Biobased 1,5-Pentanediol Derived Aliphatic-Aromatic Copolyesters: Synthesis and Thermo-Mechanical Properties of Poly(pentylene Succinate-Co-terephthalate)s and Poly(pentylene Adipate-Co-terephthalate)s

Modification of Poly(ethylene 2,5-Furandicarboxylate) with Aliphatic Polycarbonate Diols: 1. Randomnized Copolymers with Significantly Improved Ductility and High CO2 Barrier Performance

High Molecular Weight Polyesters Derived from Biobased 1,5-Pentanediol and a Variety of Aliphatic Diacids: Synthesis, Characterization, and Thermo-Mechanical Properties

Modification of Poly(ethylene furandicarboxylate) with Aliphatic Polycarbonate diols: 1. Randomnized Copolymers with Significantly Improved Ductility and High CO2 Barrier Performance

Biobased Copolyesters from Renewable Resources: Synthesis and Crystallization Behavior of Poly(decamethylene Sebacate-Co-isosorbide Sebacate)

Biobased Multiblock Copolymers: Synthesis, Properties and Shape Memory Behavior of Poly(hexamethylene 2,5-Furandicarboxylate)-b-poly(ethylene Glycol)

Synthesis, Thermal Behavior, and Mechanical Properties of Fully Biobased Poly(Hexamethylene 2,5-Furandicarboxylate-Co-Sebacate) Copolyesters

Synthesis and characterization of biobased copolyesters based on pentanediol: (1) Poly(pentylene dodecanoate‐co‐furandicarboxylate)

Synthesis and properties of high‐performance biobased liquid crystal copolyesters modified by small amount of 2,5‐furandicarboxylic acid

Synthesis and properties of high performance biobased liquid crystal polyester based on furandicarboxylic acid and sebacic acid

Tricyclic Diester and 2,5-Furandicarboxylic Acid for the Synthesis of Biobased Hydrolysis Copolyesters with High Glass Transition Temperatures

Crystallization Kinetics, Morphology, and Mechanical Properties of Novel Biodegradable Poly(Ethylene Succinate-Co-Ethylene Suberate) Copolyesters

Synthesis and properties of poly(ethylene‐co‐diethylene glycol 2,5‐furandicarboxylate) copolymers

Bio-based copolyesters poly(butylene 2,6-naphthalate-co-butylene furandicarboxylate) derived from 2,5-furandicarboxylic acid (FDCA): Synthesis, characterization, and properties

Preparation and performance exploration of 2,5‐furandicarboxylic acid‐based copolyester bioplastics: Controlling thermal properties, tensile properties, and surface hydrophilicity through composition

Synthesis and Characterization of 2,5-Furandicarboxylic Acid Poly(butanediol Sebacate-Butanediol) Terephthalate (pbset) Segment Copolyesters with Excellent Water Vapor Barrier and Good Mechanical Properties

Synthesis and Structure–Property Relationships of Novel High Molecular Weight Fully Biobased 2,5-Thiophenedicarboxylic Acid-Based Polyesters