Abstract:The Er 3+ /Yb 3+ co-doped Y 4 GeO 8 crystal powders were successfully synthesized using a high-temperature solid-phase method. The crystal structure of the obtained phosphors was confirmed to be pure Y 4 GeO 8 through X-ray diffraction (XRD) analysis. A regression equation correlating Er 3+ /Yb 3+ doping concentrations with luminescent intensity was established based on the optimized theoretical model derived from experimental design. The optimal concentrations of Er 3+ and Yb 3+ under 980 nm laser excitation were determined as 7.41 and 21.34%, respectively, while under 1550 nm laser excitation, the concentrations were 2.66 and 17.42%, respectively. The fluorescence emission spectra of the up-conversion samples were measured, revealing intense green and red emissions with peaks at 542, 546, and 654 nm under 980 nm excitation, and peaks at 546, 557, and 663 nm under 1550 nm excitation. These peaks correspond to transitions from 2 H 11/2 to 4 I 15/2 , 4 S 3/2 to 4 I 15/2 , and 4 F 9/2 to 4 I 15/2 energy levels. The relationship between up-conversion luminescence and laser operating current for the optimal samples under 980 nm and 1550 nm was investigated, uncovering that up-conversion luminescence occurs through both two-photon and three-photon processes. A detailed analysis and discussion of the up-conversion luminescence mechanisms were conducted. Furthermore, the relationship between up-conversion fluorescence and temperature for the optimal samples was studied, revealing excellent temperature-sensing characteristics under 980 nm and 1550 nm laser excitations. The calculated illumination region coordinates for the optimal samples under 980 nm and 1550 nm wavelength excitations were (0.5558, 0.4362) and (0.5256, 0.4687), respectively. The research highlights the potential of rare-earth ion-doped up-conversion luminescent materials for diverse anti-counterfeiting applications. In particular, the Y 4 GeO 8 : Yb 3+ /Er 3+ phosphors, incorporating a dual-excitation mechanism, enhance the security of anti-counterfeiting strategies in multifaceted scenarios. The study underscores the promising developments in this field.

Observation and Photoluminescence Properties of Two Er3+ Centers in CaSc2O4:Er3+, Yb3+ Upconverting Phosphor

Chemical Combustion Synthesis and Up-Conversion Properties of Er3+ Doped Yb3Al5O12 Powder

Spectroscopic Properties Of Er3+/Yb3+ Co-Doped 50sio(2)-20al(2)O(3)-30caf(2) Glass And Glass Ceramics

Effects of Er3+ and Yb3+ Concentrations on Upconversion Luminescence and Thermal Sensing Characteristics of Sc2O3:Er3+/Yb3+ Phosphors

Spectroscopic Properties of Er3+/Yb3+ Co-Doped 50sio2–20al2o3–30caf2 Glass and Glass Ceramics

Preparation of Gd2O2S:Er3+,Yb3+ phosphor and its multi-wavelength sensitive upconversion luminescence mechanism

Thermally boosted upconversion and downshifting luminescence in Sc2(MoO4)3:Yb/Er with two-dimensional negative thermal expansion

Er3+/Yb3+ Codoped Phosphor Ba3Y4O9 with Intense Red Upconversion Emission and Optical Temperature Sensing Behavior

Upconversion Luminescence of Yb3+/Tb3+/Er3+-Doped Fluorosilicate Glass Ceramics Containing Srf2 Nanocrystals

The synthesis and luminescence properties of efficient Ba5 Zn4 Y8 O21∶Er3+/Yb3+ upconversion phosphor

Impact of Sc3+-Modified Local Site Symmetries on Er3+ Ion Upconversion Luminescence in Y2O3 Nanoparticles

Experimental Optimization, Design Synthesis, and Up-Conversion Luminescence Properties of Y4GeO8: Er3+/Yb3+ Red Phosphors

Upconversion Luminescent Properties and Mechanisms of Bulk La2O2CN2: Er3+/Yb3+ Phosphors

Upconversion Photoluminescence Properties of SrY2O4:Er3+,Yb3+ under 1550 and 980 Nm Excitation

Excellent red upconversion luminescence in GdLaO3:Er3+/Yb3+/Sc3+ under 980 nm laser excitation

Synthesis and Luminescence Properties of Ca3Y2Si3O12∶Tm3 + , Yb3 + Upconversion Phosphors

Effect of Er and Yb Doping Concentration on the Luminescent Properties of Y<sub>2</sub>O<sub>2</sub>S:Yb, Er Phosphors

Up-conversion Luminescence and Thermal Sensing Properties of LuYO3: Er3+/Yb3+ Phosphor

Upconversion Properties and Temperature-Sensing Behaviors of Alkaline-Earth-Metal Scandate Nanocrystals Doped with Er 3+ /Yb 3+ Ions in the Presence of Alkali Ions (Li + , Na + , and K + )

Effects of Sc3+ ions on local crystal structure and up-conversion luminescence of layered perovskite NaYTiO4: Yb3+/Er3+

High quenching concentration of the CaLuAlO4:Er3 + upconversion phosphor with short-range energy migration