High Hiding Power and Weather Durability of Film-Coated Titanium Dioxide Particles with a Yolk-Shell Structure

Yong Liang,Keyi Yu,Jiuren Xie,Qinzhong Zheng,Ting-Jie Wang

DOI: https://doi.org/10.1016/j.colsurfa.2017.02.046

2017-01-01

Colloids and Surfaces

Abstract:High hiding power and weather durability are the key characteristic indices of the high-performance pigmentary titanium dioxide (TiO2). The film-coated TiO2 particles with a yolk-shell structure of silica were prepared by surface-protected etching with polyvinyl pyrrolidone. The hiding power of the TiO2 particles with the yolk-shell structure was 90.6, which is significantly higher than the hiding power of 87.7 for the dense film-coated TiO2 particles with the same amount of coating (20%). However, the TiO2 particles with the yolk-shell structure have low weather durability. The apparent degradation rate constant Kapp for rhodamine-B had a high value of 13.2. An improvement was made by coating a dense MgO film on the TiO2 particles first, and then coating a yolk-shell structure. The hiding power of the TiO2 particles with the improved yolk-shell structure reached 90.6, and the weather durability was significantly increased as the apparent degradation rate constant Kapp decreased to 2.2, reaching the excellent weather durability of the TiO2 particles with 5 wt% dense film coating (Si3 + Al2), which is a common product in industry (Kapp = 1.8). For the same indices of hiding power and weather durability, the TiO2 particles with the improved yolk-shell structure obviously decreased the consumption of TiO2, compared with the dense SiO2-coated TiO2 particles (TiO2@SiO2). It is inferred that the void in the yolk-shell structure increased the light reflectivity of the TiO2 particles by increasing the difference of the refractive index between the core TiO2 and the surroundings, and the dense MgO film increased the weather durability of the TiO2 particles.