Abstract:The 2195 Al-Cu-Li alloy is widely utilized in the aerospace industry due to its lightweight nature and high strength. Consequently, gaining a comprehensive understanding of techniques to enhance its microstructural and mechanical properties is crucial for the consistent production of reliable and high-strength aerospace components. In this investigation, a pristine 2195 industrial ingot was subject to three distinct forging pretreatments: PT1, which involved a direct three upsetting and three stretching (3U3S) process; PT2, which combined double stage homogenization (DH) with 3U3S; and PT3, which involved DH along with six upsetting and six stretching (6U6S). Subsequent warm deformation and T8 aging treatment were applied to the pretreated forgings. The microstructure evolution during the processes and the final mechanical properties in three orthogonal dimensions were examined. The findings revealed that the combination of DH and multi-dimensional forging (MDF) facilitated the dissolution of non-equilibrium phases to a greater extent. Consequently, the main strengthening phase transformed from the T 1 + δ` phase observed in PT1 to the denser T1 + little θ` phase observed in PT2 and PT3 after T8 aging treatment. Notably, the tensile strength and yield strength of PT2 and PT3 specimens increased by 20-30 MPa in all three directions. Moreover, the MDF process accelerated the recrystallization behavior from PT1 to PT3, resulting in a gradual reduction in the average grain size of the pretreated samples from 356 μm to 186 μm. Following warm forging and T8 aging, the grains exhibited a finer and equiaxed structure. Additionally, the coarse phase was identified as the primary source of transgranular cracking. The coarse phases within the matrix became more homogeneous and finer from PT1 to PT3, with a gradual decrease in their area fraction. On the fracture surfaces, the aggregation of coarse phases diminished. Consequently, the elongation in the z-direction improved, and the elongation anisotropy and standard deviation decreased in all three directions for PT3 specimens. The findings presented in this study provide valuable insights into the high-performance manufacturing of Al-Cu-Li alloys.

Grain Refinement of Aluminum Alloy Bar by A Modified Rap Process for Semi-Solid Forming

Effect of cross-sectional reduction ratio on microstructure evolution of semi-solid 7075 aluminum alloy prepared by RFSIMA process

Grain Refinement Mechanism of 5A06 Aluminum Alloy Sheets during Cold Rotary Forging

Microstructure characteristics of the 2A50 aluminum alloy in radial forging and isothermal treatment conditions

Thermomechanical processing of AA6061 billets for semi-solid forming

Deformation Characteristics and Constitutive Equations for the Semi-Solid Isothermal Compression of Cold Radial Forged 6063 Aluminium Alloy

Spinning Process of 2219 Aluminum Alloy Tubes for Used in Hydroforming

Effect of radial shear rolling on grain refinement and mechanical properties of the Al–Mg–Sc alloy

Recrystallization process of hot-extruded 6A02 aluminum alloy in solid and semi-solid temperature ranges

Efficiently manufacturing large-scale isotropic Al7075 alloy sheets with submicron grain by multidirectional rotary forging

Refinement mechanism of centimeter-grade coarse grains in as-cast Ti 2 AlNb-based alloy during multi-directional forging

Investigation of the Penetration Performance of the Radial Forging Process for Wrought Aluminium Alloy

Effect of Heating Process on Semi-solid Microstructure of Cold Rolled 6061 Aluminum Alloy

Comprehensive study of hot compression behaviors and microstructure evolution of solutionized 6082 aluminum alloy extruded bar

Processability of A6061 Aluminum Alloy Using Laser Powder Bed Fusion by In Situ Synthesis of Grain Refiners

Microstructural evolutions and mechanical properties of 6082 aluminum alloy part produced by a solution-forging integrated process

Grain refinement in semi-solid metal processing: current status and recent development

Enhanced grain refinement and texture weakening in Al–Mg–Si alloy through a novel thermomechanical processing

Effect of forging pretreatment on the microstructures and mechanical properties of the Al-Cu-Li alloy

Preparation of high performance 5083 aluminum alloy by alternate ring-groove pressing and torsion

Recrystallization of Hot-Rolled 2A14 Alloy during Semisolid Temperature Annealing Process