Effect of Trimethylolpropane Triacrylate Cross-Linkages on the Thermal Stability and Char Yield of Poly (methyl Methacrylate) Nanocomposites

Logan C. Hatanaka,Qingsheng Wang,Zhengdong Cheng,M. Sam Mannan

DOI: https://doi.org/10.1016/j.firesaf.2016.12.004

IF: 3.78

2017-01-01

Fire Safety Journal

Abstract:Using an in-situ polymerization method, poly (methyl methacrylate) (PMMA) cross-linked by trimethylolpropane triacrylate (TMPTA) was embedded with nanosilica, aluminum oxide, or modified montmorillonite to produce various cross-linked nanocomposites. The same three nanofillers were also embedded into PMMA without TMPTA cross-linkages to quantify the effect of TMPTA cross-linkages on the thermal stability and char yield of nanocomposites. Data from Thermogravimetric Analysis (TGA) and Derivative Thermogravimetric Analysis (DTG) were used to show that cross-linking and nanofiller content act synergistically to improve the thermal stability of PMMA, increasing the on-set of degradation by nearly 100°C. The increase in thermal stability was attributed to the elimination of low temperature end initiated polymer unzipping by TMPTA cross-linkages and simultaneous stabilization of remaining degradation reactions due to nanofiller content. Char formed during a fire accumulates on the surface of the nanocomposite, forming a barrier that protects any unburned material below the surface. The DTG data showed nanocomposites containing 1wt% silica in PMMA cross-linked by TMPTA produced 14.1% char residues, while nanocomposites without TMPTA cross-linkages required five times the mass of nanofiller to achieve similar yields.