Abstract:ZL205A alloys tend to form disordered and defective microstructure due to the large solidification intervals and multi-phase. Accordingly, finding ways to effectively optimize the microstructure and mechanical performance is of great significance. In this regard, the coupling of travelling magnetic fields (TMF) with unidirectional solidification was used to continuously regulate the mushy zones of ZL205A alloys. Additionally, experiments are combined with simulations to systematically reveal the mechanisms on the optimizations at each stage of solidification process. Current findings demonstrate that different directional strong melt flows generated by TMF are responsible for these optimizations. Additionally, the effects of TMF on microstructure are different at each stage of solidification process. Specifically, downward TMF coupled with unidirectional solidification can refine and uniform the microstructure, decrease the formation of precipitation, promote the growth consistency of matrix phase α-Al growing along the <001> crystal orientation, reduce the secondary dendrites and overlaps between dendrites, eliminate the shrinkage defects, and increase the ultimate tensile strength, yield strength, elongation and hardness from 198.3 MPa, 102.2 MPa, 7.5 % and 82.3 kg mm−2 without TMF to 225.5 MPa, 116.1 MPa, 13.6 % and 105.2 kg mm−2. Contrastively, although upward TMF can reduce Al3Ti and refine α-Al, it increases the formation of Al6Mn, Al2Cu, secondary dendrites, overlaps between dendrites, and shrinkage defects; then it deflects and disorders the growth of α-Al, further to decrease the overall performance of alloys.

Effect of Microadditives on Center Segregation and Mechanical Properties of High-Strength Low-Alloy Steels

Microstructure Evolution and Precipitation Strengthening Behaviour of Additively Manufactured High-speed Steels

Effect of Adding Ceramic Particles on Grain Refining in Low Carbon Microalloy Steel

Effect of Zr-Ti Combined Deoxidation on the Microstructure and Mechanical Properties of High-Strength Low-Alloy Steels

Strengthening Effect of ZrC Particles on Low-Carbon Microalloy Steel

Synergistic Effect of Alloying on the Strength and Ductility of High Carbon Pearlitic Steel

Synergistic optimization in microstructure and mechanical properties of low carbon steel via trace amount of nano-sized TiC-TiB2

Titanium microalloying of steel: A review of its effects on processing, microstructure and mechanical properties

Microstructural Refinement and Strain Hardening Behavior in Low-Density Ultrafine Pearlite Steel

Effect of Zr Treatment on Inclusion and Solidification Microstructure in Ti Deoxidized Low Carbon Microalloyed Steel

Optimizing Microstructure, Shrinkage Defects and Mechanical Performance of ZL205A Alloys Via Coupling Travelling Magnetic Fields with Unidirectional Solidification

CONTROL AND DESIGN OF MICROSTRUCTURE IN STEELS (Ⅱ)

Effect of Rare Earth Elements on Microstructure and Tensile Behavior of Nb-Containing Microalloyed Steels

Microsegregation Influence on Austenite Formation from Ferrite and Cementite in Fe–C–Mn–Si and Fe–C–Si Steels

Micro-alloying effects of Ni on the microstructure and mechanical properties of an Al-Zn-Mg-Cu-Sc-Zr alloy

Effect of Micro-Alloyed Ti on Inclusions Modification

Synergistic Effect of Al and Ni on Microstructure Evolutions and Mechanical Properties of Fe-Mn-Al-C Low-Density Steels

Effect of Alloying Powders on Microstructure and Mechanical Properties of Aluminum Alloy Arc Additive Manufacturing

Effect of Minor Sc and Fe Co-Addition on the Microstructure and Mechanical Properties of Al-Cu Alloys During Homogenization Treatment

Effect Of Coupled Annular Electromagnetic Stirring And Intercooling On The Microstructures Macrosegregation And Properties Of Large-Sized 2219 Aluminum Alloy Billets

Improvements in Microstructure Homogenization and Mechanical Properties of Diffusion-Alloyed Steel Compact by the Addition of Cr-Containing Powders