Abstract:Improving the specific oxygen reduction reaction (ORR) activity (SOA) of platinum catalysts is a promising way to reduce the amount of platinum required for the cathode in polymer electrolyte fuel cells. In this study, we compared the SOA of Pt catalysts loaded on two types of Ketjen Black: pristine (KB) and a sample heat treated at 1500 °C (KB1500). In addition, we characterized the platinum deposited on the carbon and compared the durability of these catalysts against potential cycling. The platinum catalyst loaded on KB1500 (Pt/KB1500) showed doublet hydrogen adsorption peaks at 0.12 V vs. RHE, observed by cyclic voltammetry, and the formation of atomically disperse platinum catalysts, which formed a cloud‐like distribution with platinum atoms. Such a cloud‐like distribution has not been observed for Pt/KB previously, and the higher SOA of the Pt/KB1500 catalyst was due to the presence of the finely dispersed cloud‐like platinum species. The differences in the surface structure of the carbon supports were investigated using X‐ray diffraction, Raman scattering, electron spin resonance, and temperature‐programmed desorption. The characterization revealed that KB1500 has continuous larger graphitic layers with point defects and holes, whereas KB has smaller graphitic layers whose edge sites are decorated with oxygen functional groups and hydrogen atoms. The durability of Pt/KB1500 in potential cycling tests was determined by cyclic voltammetry between 0.6 and 1.0 V vs. RHE for 10,000 cycles. These measurements revealed the high SOA and survival of the characteristic hydrogen adsorption peak at 0.12 V vs. RHE. Here, we demonstrate the improvements in the specific ORR activity and the potential cycling durability of the Pt catalysts supported on a heat‐treated Ketjen Black. The formation of cloud‐like atomically dispersed Pt species was detected on the support by STEM‐HAADF. Detailed structural analyses of the carbon supports were conducted by using high temperature TPD technique.

Study on the Mechanism and Kinetics of Oxygen Reduction Reaction on 3D Porous Platinum Film Constructed Using Colloidal Crystal Template

Mechanisms of Electrocatalysis of Oxygen Reduction by Metal Porphyrins in Trifluoromethane Sulfonic Acid Solution

Enhanced Oxygen Reduction Activity of Platinum Micropore

Intermetallic Pd3Pb square nanoplates as highly efficient electrocatalysts for oxygen reduction reaction

(Invited) How Oxygen-Containing Intermediates and Surface Charge Regulate Oxygen Reduction Reaction of Platinum Electrocatalysts

Pt3Re Alloy Nanoparticles As Electrocatalysts for the Oxygen Reduction Reaction

Three-Dimensional Ordered Macroporous Platinum-Based Electrode for Methanol Oxidation

Theoretical Investigation of the Oxygen Reduction Reaction over Platinum Catalysts Supported by Multi‐Edged Vertically Aligned Carbon Nanofiber for Electrocatalyst Preparation

Hierarchical Porous Pt/ZrO2 Nanoframework for Efficient Oxygen Reduction Reaction

Pt-decorated Nanoporous Gold Film Prepared Via Solid-Phase Reaction for Enhancing Oxygen Reduction Electrocatalysis

An elegant 3D-ordered hierarchically porous framework to anchor Pt nanocrystals for durable oxygen reduction reaction

Unifying Theoretical Framework for Deciphering the Oxygen Reduction Reaction on Platinum.

A polyacrylonitrile copolymer-silica template for three-dimensional hierarchical porous carbon as a Pt catalyst support for the oxygen reduction reaction.

Alternate assemblies of platinum nanoparticles and metalloporphyrins as tunable electrocatalysts for dioxygen reduction.

Hierarchical Porous Pt/ZrO 2 Nanoframework for Efficient Oxygen Reduction Reaction

Two-Dimensional Porous PtPd Nanostructure Electrocatalysts for Oxygen Reduction Reaction

Enhanced Electrochemical Oxygen Reduction By Modulating Electronic Structures of Platinum Nanoparticles By Nitrogen-Introduced Carbon Support

Construction and Regulation of a Surface Protophilic Environment to Enhance Oxygen Reduction Reaction Electrocatalytic Activity

Platinum Nanoparticles Supported on Different Substrates as Electrocatalysts for Oxygen Reduction Reaction

Recent Development of Platinum-Based Nanocatalysts for Oxygen Reduction Electrocatalysis

Electrochemical Properties of an Atomically Dispersed Platinum Catalyst Formed on a Heat-treated Carbon Support