Abstract:Nitrogen-enriched porous carbon has been a promising material for CO2 capture in the recent decades. To enhance the performance of CO2 adsorption, both an N-active site and the textural properties are crucial determinants. Herein, ultra-microporous carbon with N-active species was prepared using two synthesis procedures: 1) one-step carbonization of a polybenzoxazine (PBZ) precursor at 800 °C, and 2) the CO2 activation process at 900 °C. The activated porous carbon had the higher specific surface area (943 m2/g) and a total pore volume (0.51 cm3/g) compared to un-activated porous carbon (335 m2/g and 0.19 cm3/g, respectively). In addition, the presence of N-active species such as pyridine-N, secondary-N, pyridone-N, and oxide-N in the carbon structures could be clearly observed in the high-resolution XPS spectra. The CO2 adsorption measurement was performed at 30 and 50 °C under a wide range of pressures (1-7 bar). The maximum amount of CO2 uptake was ca. 3.59 mmol/g for the activated porous carbon operated at 30 °C and a CO2 pressure of 7 bar, which was due to the high specific surface area and the large micropore volume. Specifically, carbon with a 3D interconnected pore structure, derived from the sol-gel process of the PBZ precursor, exhibited good structural stability and consequently led to better absorption capability under the high atmospheric pressure of CO2. The enhanced CO2 adsorption capability for the as-prepared porous carbon was based on two mechanisms: physisorption as a result of textural properties and chemisorption as a result of the acid-base interaction between the basic N functionality and the acidic CO2 gas. All results suggested that ultra-microporous carbon with N-active species prepared from polybenzoxazine is a promising adsorbent for CO2 capture and storage, which can be used at a wide range of pressures and in many applications e.g. flue gas adsorption and natural gas production.

One-Pot Carbonization Enrichment Of Nitrogen In Microporous Carbon Spheres For Efficient Co2 Capture

Preparation of cage-like nano-CaCO3 hollow spheres for enhanced CO2 sorption

Nitrogen-doped hierarchically porous carbon spheres for low concentration CO2 capture

Structurally Designed Synthesis of Mechanically Stable Poly(benzoxazine-co-resol)-Based Porous Carbon Monoliths and Their Application As High-Performance CO2 Capture Sorbents

One-Step Synthesis of Microporous Carbon Monoliths Derived from Biomass with High Nitrogen Doping Content for Highly Selective CO2 Capture.

Resorcinol–formaldehyde Resin-Based Porous Carbon Spheres with High CO2 Capture Capacities

One-Pot Synthesis of Melamine Formaldehyde Resin-Derived N-Doped Porous Carbon for CO2 Capture Application

Facile synthesis of porous carbon nitride spheres with hierarchical three-dimensional mesostructures for CO 2 capture

Synthesis of hollow micro-mesoporous nitrogen-doped carbon nanoparticles for enhanced CO2 capture

Biomass-based N-rich porous carbon materials for CO2 capture and in situ conversion.

Facile Synthesis of MOF-5-derived Porous Carbon with Adjustable Pore Size for CO2 Capture

High yield nitrogen-doped carbon monolith with rich ultramicropores prepared by in-situ activation for high performance of selective CO2 capture

Synthesis of nitrogen-doped hollow carbon nanospheres for CO2 capture.

N-doped porous carbon derived from macadamia nut shell for CO 2 adsorption

Metal-free Core-Shell Structured N-doped Carbon/carbon Heterojunction for Efficient CO2 Capture

Nitrogen-rich hollow carbon microspheres with tunable shell thicknesses for enhanced CO2 adsorption

Sustainable Biomass Glucose-Derived Porous Carbon Spheres with High Nitrogen Doping: As a Promising Adsorbent for CO2/CH4/N2 Adsorptive Separation

One-Pot Synthesis of N-Rich Porous Carbon for Efficient CO2 Adsorption Performance

Enhanced CO2 capturing over ultra-microporous carbon with nitrogen-active species prepared using one-step carbonization of polybenzoxazine for a sustainable environment

One-step, template-free synthesis of highly porous nitrogen/sulfur-codoped carbons from a single protic salt and their application to CO2 capture

Development and CO2 capture of nitrogen-enriched microporous carbon by coupling waste polyamides with lignocellulosic biomass