The effects of elements doping on transport and thermoelectric properties of Sr3Ti2O7
R. R. Sun,Xiaoying Qin,Liangliang Li,Desong Li,Jie Zhang,Yongsheng Zhang,Chunjuan Tang
DOI: https://doi.org/10.1016/j.jpcs.2014.01.002
IF: 4.383
2014-01-01
Journal of Physics and Chemistry of Solids
Abstract:The Ruddlesden–Popper (RP) phase compounds (Sr0.95R0.05)3Ti2O7 (R=Er, Y, Dy, Gd, Eu, Sm, Nd and La) were prepared, and their transport and thermoelectric properties were investigated. The results indicate that high-T electrical resistivity ρ (300K<T<1000K) increases monotonically with temperature and basically has a relation ρ∝TM, with M varying from 0.91 to 1.92 at temperatures T>~650K, suggesting acoustic phonon scattering is dominant. At low temperatures (5K<T<300K), ρ for (Sr0.95R0.05)3Ti2O7 (R=Nd and La) decreases monotonously with decreasing temperature, whereas ρ for (Sr0.95R0.05)3Ti2O7 (R=Er, Y, Dy, Gd, Eu and Sm) decreases first, and then increases instead as T decreases to a critical temperature Tc. Moreover, electrical conductivity σ∝T1/2 holds at lower temperatures, indicating that the electron–electron interaction caused by the presence of disorder dominates the transport process at the low temperatures. Besides, experiments show that at T<~400K the lattice thermal conductivity of the doped compounds basically decreases with increase of the atomic mass of dopants. Generally, the figure of merit (ZT) at 1000K increases first, and then decreases with the increase of the dopants' ionic radius, and the largest ZT is achieved in (Sr0.95Gd0.05)3Ti2O7 mainly owing to its lower lattice thermal conductivity.