Abstract:The Mg-11Gd-2Zn-0.4Zr (GZ112K, wt.%) alloys fabricated by selective laser melting (SLM) still contain some hard and brittle beta-(Mg,Zn)(3)Gd eutectic phase with an area fraction of 4.86% despite the ultra-fast cooling rate of SLM process, so post heat treatment is necessary. The effects of different solution conditions and aging heat treatment on microstructure and mechanical properties of the SLMed GZ112K alloys were systematically analyzed. The results show that the optimized solution condition (400 degrees C x 12 h) for the SLMed GZ112K alloys can not only transform hard and brittle beta-(Mg,Zn)(3)Gd eutectic phase into relatively softer lamellar 14H type long period stacking order (LPSO) structure leading to the improved elongation (EL) of the SLM-T4 alloys, but also retain the fine grains of the SLMed GZ112K alloys to a large extent with a small average grain size of 3.1 mu m in the SLM-T4 state contributing to the high yield strength (YS) of the SLM-T4 and SLM-T6 GZ112K alloys. After peak aging heat treatment, basal gamma ' precipitates or lamellar 14H-LPSO structure and dense prismatic elliptical 13 ' precipitates coexist in the SLM-T6 GZ112K alloys. As a result, the SLM-T6 GZ112K alloys exhibit YS of 343 +/- 9 MPa, ultimate tensile strength (UTS) of 371 +/- 4 MPa and EL of 4.0 +/- 0.05%, while those of the SLMed GZ112K alloys are 332 +/- 3 MPa, 351 +/- 5 MPa and 8.6 +/- 1.0%. The ultra-high YS of SLM-T6 GZ112K alloys results from the fine grain strengthening, the precipitation strengthening from 13 ' aging precipitates, the secondary phase strengthening from LPSO structure and X phase and the extra composite strengthening from the coexistence of basal and prismatic precipitates. The findings indicate that appropriate post heat treatment is an effective scheme for modifying microstructure and mechanical properties of the SLMed alloys.

Selective Laser Melting of Al-Zn-Mg-Cu: Heat Treatment, Microstructure and Mechanical Properties

Selective Laser Melting of Al-Cu-Mn-Mg Alloys: Processing and Mechanical Properties

A Study on Sc- and Zr-modified Al–Mg Alloys Processed by Selective Laser Melting

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

Processing Technologies and Properties of Cu-10Sn Formed by Selective Laser Melting Combined with Heat Treatment

Selective laser melting of Al-3.48Cu-2.03Si-0.48Sc-0.28Zr alloy: Microstructure evolution, properties and metallurgical defects

Achieving Ultra-High Strength and Ductility in Mg–9Al–1Zn–0.5Mn Alloy Via Selective Laser Melting

Selective Laser Melting of Al-7Si-0.5 Mg-0.5Cu: Effect of Heat Treatment on Microstructure Evolution, Mechanical Properties and Wear Resistance

Selective laser melting of Cu–Cr–Zr copper alloy: Parameter optimization, microstructure and mechanical properties

Superior mechanical properties of a selective-laser-melted AlZnMgCuScZr alloy enabled by a tunable hierarchical microstructure and dual-nanoprecipitation

Effect of laser power on microstructures and properties of Al-4.82Mg-0.75Sc-0.49Mn-0.28Zr alloy fabricated by selective laser melting

Selective Laser Melting of Mg-Zn Binary Alloys: Effects of Zn Content on Densification Behavior, Microstructure, and Mechanical Property

Enhanced hardness and moderate thermal conductivity of Cu-2.4Ni-0.7Si alloy processed via selective laser melting followed by suitable heat treatment

Mechanical Properties of High Mg-Content Al-Mg-Sc-Zr Alloy Fabricated by Selective Laser Melting

Tensile property and microstructure of Al−4.77Mn−1.37Mg−0.67Sc−0.25Zr alloy under different selective laser melting processing parameters

Effect of T6 Heat Treatment on the Surface Tribological and Corrosion Properties of AlSi10Mg Samples Produced by Selective Laser Melting

Effect of Heat Treatment on Microstructure Evolution and Mechanical Properties of Selective Laser Melted Mg-11Gd-2Zn-0.4Zr Alloy

Selective laser melting of CuCrZr alloy: processing optimisation, microstructure and mechanical properties

Microstructure, heat treatment and mechanical properties of TiB2/Al–7Si–Cu–Mg alloy fabricated by selective laser melting

Microstructure, metallurgical defects and hardness of Al–Cu–Mg–Li–Zr alloy additively manufactured by selective laser melting

The AlSi10Mg Samples Produced by Selective Laser Melting: Single Track, Densification, Microstructure and Mechanical Behavior