Abstract:Polyacrylonitrile (PAN) precursor nanofibers are prepared by traditional electrospinning and the centrifugal spinning, respectively. The nanofiber bundles are drawn in hot air with a constant force into 1 and 3 times of the original length. Subsequently, the crystalline structure, orientation, morphology, diameter of PAN nanofibers before and after drawing treatment were characterized by WAXD and SEM. The results show that: (1) the efficiency of centrifugal-electrospinning is far higher (120 times) than that of electrospinning (fluid flow rate of centrifugal-electrospinning: 2 mL/min, fluid flow rate of electrospinning: 1 mL/h). (2) Despite a low crystallinity from centrifugal spinning or electrospinning (the crystallinity of the PAN nanofiber precursor by centrifugal spinning is 25%, while that by electrospinning is 10.6%). PAN precursor nanofibers prepared by centrifugal spinning have certain orientation (60.5%); while those prepared by electrospinning have almost no orientation; (3) Hot-air-drawing with a constant force (1.00 N) contributes to a higher crystallinity (centrifugal spinning: 45.8%, electrospinning: 36.2%) and orientation (centrifugal spinning: 72.5%, electrospinning: 59.8%) for the PAN nanofibers. Moreover, increased drawing temperature and force results in a decrease in the diameter of the PAN nanofiber bundles (the diameter of PAN nanofibers prepared by centrifugal spinning decreases from 675 nm to 510 nm; while that by electrospinning decreases from 460 nm to 355 nm). Compared with the slight effect of the spinning process on crystalline structure and orientation, the hot-air drawing treatment significantly promotes the crystalline and orientation. The centrifugal force is helpful to eliminate the whip phenomenon and to make a full drawing of jet flow, finally leading to a higher certain orientation for the polymer chains of PAN nanofibers.

Structures and mechanical properties of plied and twisted polyacrylonitrile nanofiber yarns fabricated by a multi-needle electrospinning device

Fabrication of Continuous Electrospun Nanofiber Yarns with Direct 3d Processability by Plying and Twisting

Structures and Properties of Polyacrylonitrile/Graphene Composite Nanofiber Yarns Prepared by Multi-Needle Electrospinning Device with an Auxiliary Electrode.

Construction and Mechanical Property of High Alignment Polyacrylonitrile Nanofiber Filaments using a Multi-needle Electrospinning Device

Investigation of Post-Spinning Stretching Process on Morphological, Structural, and Mechanical Properties of Electrospun Polyacrylonitrile Copolymer Nanofibers

Effects of Chemical Composition and Post-Spinning Stretching Process on the Morphological, Structural, and Thermo-Chemical Properties of Electrospun Polyacrylonitrile Copolymer Precursor Nanofibers

Enhanced Mechanical Performance of Electrospun Graphene/Polyacrylonitrile (PAN) Composite Microfibrous Yarns Via Post-Processing

Nanostructured Electrospun Hybrid Graphene/Polyacrylonitrile Yarns

Strip twisted electrospun nanofiber yarns: Structural effects on tensile properties

Mechanical and Electrical Properties of the Pa6/Swnts Nanofiber Yarn by Electrospinning

Microstructural Evolution and Mechanical Investigation of Hot Stretched Graphene Oxide Reinforced Polyacrylonitrile Nanofiber Yarns

High conductivity electrospun carbon/graphene composite nanofiber yarns

Non-Coagulant Spinning of High-Strength Fibers from Homоpolymer Polyacrylonitrile Synthesized via Anionic Polymerisation

A Novel Method to Fabricate High Strength Nanofiber Filaments: Morphology, Crystalline Structure, and Thermal and Mechanical Properties

Highly-efficient Fabrication and Crystallinity and Orientation of Polyacrylonitrile Nanofibers

Wet Twisting in Spinning for Rapid and Cost‐Effective Fabrication of Superior Carbon Nanotube Yarns

Enhancing Crystallinity and Orientation by Hot-Stretching to Improve the Mechanical Properties of Electrospun Partially Aligned Polyacrylonitrile (PAN) Nanocomposites

Structural Features of Polyacrylonitrile-Based Carbon Fibers

Microstructure and Electrochemical Properties of Polyacrylonitrile-Based Carbon Micro- and Nanofibers Fabricated by Centrifugal Spinning

Carbon nanotube yarns with high tensile strength made by a twisting and shrinking method.

Effect of Nanocrystalline Cellulose Addition on Needleless Alternating Current Electrospinning and Properties of Nanofibrous Polyacrylonitrile Meshes