Abstract:A simple spray approach to fabricate superhydrophobic coatings on tile and glass substrates is presented. Commercial available polyphenylene sulfide (PPS) and hydrophobic silica (H-SiO(2)) powder were suspended in ethanol and the mixed suspensions were spray on substrates. After dried at different temperatures, surface coatings with different hydrophobicity were obtained. By observing the surface morphologies with scanning electron microscope (SEM) and atomic force microscope (AFM), and measuring water contact angles with a contact angle system, factors affecting the morphology, roughness and contact angle of the surface coatings, such as thermal treatment temperature and the weight ratio of H-SiO(2) to PPS, were investigated in detail. With the increase of the thermal treatment temperature, both the surface roughness and the contact angle increased when the temperature was lower than 280 degrees C. As the weight ratio of H-SiO(2) to PPS rose from 1: 10 to 1:1, more H-SiO(2) powders accumulated on the surface, leading to a significant increase of hydrophobicity. The surface coating obtained at 280 degrees C with the weight ratio of H-SiO(2) to PPS 1:1 showed a water contact angle higher than 150 degrees and a sliding angle lower than 4, exhibiting fascinating superhydrophobic properties. The surface coating could remain superhydrophobicity upon a further increase in thermal treatment temperature or the amount of H-SiO(2) powder. Moreover, the surface coatings showed high contact angles, larger than 150, for all the solutions with pH ranging from 1 to 14. The abrasion resistant property of the as-prepared superhydrophobic surface coating was tested using a homemade setup. Being scraped by freely-falling sands, the superhydrophobic coating could keep its high hydrophobicity, while a commercial hydrophobic coating transformed from hydrophobicity to hydrophilicity. This result implied our superhydrophobic surface coating was very stable. Moreover, chalk powders on the superhydrophobic surface coatings could easily be washed off with water, indicating good self-cleaning properties. The presented approach is convenient and can be potentially applied in fabrication of superhydrophobic surfaces in large scale.

Preparation and characterization of antiglare waterborne polyurethane

The Preparation and Characterization of Uniform Nanoporous Structure on Glass

Tuning the optical properties of high solid waterborne polyurethane from matt to anti-glare

Bio-Based Waterborne Polyurethane Coatings with High Transparency, Antismudge and Anticorrosive Properties

Highly Transparent and Highly Hydrophobic Coating for Outdoor Camera Window Glass: Fabrication, Transparency, and Hydrophobicity

Fabrication of a robust zwitterionic coating on glass with anti-fogging, anti-frosting, self-cleaning and antibacterial properties via UV-induced grafting polymerization

Fabrication of UV-curable waterborne polyurethane coatings with self-cleaning, anti-graffiti performance, and corrosion resistance

Preparation and characterization of hydrophobic waterborne polyurethane self‐matting coating

Transparent Superhydrophobic and Self-Cleaning Coating

Preparation of high-performance polyurethane-polyacrylate coatings based on hyperbranched structure and application in anti-ultraviolet film

Preparation, Characterization, and Property Analysis of Environmentally Friendly Waterborne Polyurethane-Acrylate

Self-antiglare Waterborne Coating with Superior Mechanical Robustness and Highly Efficient Room-Temperature Self-Healing Capability

A Facile Approach to UV-curable Super-Hydrophilic Polyacrylate Coating Film Grafted on Glass Substrate

Ultraviolet-cured polyurea-polyurethane acrylate/polysiloxane hybrid anti-fouling coatings with superior mechanical properties, transparency, and durability

Fabrication of ultra-smooth hybrid thin coatings towards robust, highly transparent, liquid-repellent and antismudge coatings

Preparation of matte, abrasion‐resistant and anti‐fouling waterborne UV‐curable coating and its application in electronic product shells

Preparation and Properties of Waterborne Polyurethane/Antimony Doped Tin Oxide Nanocomposite Coatings Via Sol-Gel Reactions

Preparation, Thermal Property and Morphology Analysis of Waterborne Polyurethane-Acrylate

Waterborne Liquid-like Coatings with High Transparency, Superior Scratch Resistance, and Antismudge Properties

Preparation and Characterization of a Self -Matting Coating Based on Waterborne Polyurethane-Polyacrylate Hybrid Dispersions

PREPARATION AND PROPERTIES OF SUPERHYDROPHOBIC POLYPHENYLENE SULFIDE COMPOSITE COATINGS