Abstract:For concrete structures exposed to frost attack, cracks, or microcracks induced by freeze-thaw cycling can format interconnecting flow paths and allow more water or chloride ions to penetrate into the bulk concrete. It will subsequently facilitate further deterioration of concrete structures and accelerate the corrosion of embedded reinforced steel bars. Moreover, in reality most concrete structures are rarely fully saturated, so that chloride transportation in unsaturated concrete must be studied with respect to the water moving process in order to cover the real existing service conditions. In the current work, a numerical simulation method based on the mesoscale composite structure of concrete, named the lattice network model, is established to analyze the penetration property of concrete; especially the effects of microcracking induced by freeze-thaw damage on the unsaturated flow behavior are investigated. In the mesoscale model, concrete is treated as a three-phase composite material consisting of coarse aggregates, mortar matrix, and interfacial transition zone (ITZ) between the aggregate and the mortar matrix. The diffusivities of each phase, (i.e., water and chloride diffusion coefficients) is separately characterized and quantified in terms of the published test results. The unsaturated flow theory for capillary water absorption and chloride transport is employed to simulate the ingress of water and chloride ions into concrete. It is found that the water absorption and chloride penetration are substantially influenced by the frost action, and the cumulative absorbed water and chloride penetration depth are increased with the increase of freezing-thawing cycles (FTCs). Furthermore, the numerical predictions about water absorption and chloride profiles are compared with the experimental measurements. The comparisons indicate that numerical predictions agree very well with the test data.

Prediction of Mass Transport in Cracked-Unsaturated Concrete by Mesoscale Lattice Model

Coupled lattice discrete particle model for the simulation of water and chloride transport in cracked concrete members

A Numerical Study on Chloride Migration in Cracked Concrete Using Multi-Component Ionic Transport Models

Model of Chloride Penetration into Cracked Concrete Subject to Drying–wetting Cycles

Mesoscale Modeling of Chloride Penetration in Unsaturated Concrete Damaged by Freeze-Thaw Cycling

Chloride transport in cracked concrete under wet-dry cycling condition

Mesoscale Modelling of the Chloride Diffusion in Cracks and Cracked Concrete

Modeling of chloride ions diffusion in cracked concrete

Mesoscale Simulation of Chloride Diffusion in Concrete Subjected to Flexural Loading

MECHANISM AND MATHEMATIC MODELING OF CHLORIDE PERMEATION IN CONCRETE UNDER UNSATURATED STATE

Numerical Study on Cracking and Its Effect on Chloride Transport in Concrete Subjected to External Load

Mesoscopic Simulation of Chloride Ions Diffusion in Frost-Damaged Concrete

Water Transport in Unsaturated Cracked Concrete under Pressure

Influence of Cracks on Chloride Diffusivity in Concrete: A Five-Phase Mesoscale Model Approach

Numerical Simulation of Three-Dimensional Crack Features and Chloride Ion Transport in Unsaturated and Damaged Mortar

Modelling the corrosion mechanism of steel bars in chloride-contaminated concrete with transverse cracks

Simulation of Chloride Diffusivity for Cracked Concrete Based on RBSM and Truss Network Model

Damage Based Constitutive Model for Predicting the Performance Degradation of Concrete

Chloride ingression in cracked concrete under saturated state

Numerical Study of Multi-species Transport in Cracked Concrete Under External Load

A Mesoscale Three-Dimensional Moisture Transport Model in Concrete