Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Eu$lt;sup$gt;3+$lt;/sup$gt; Activated Y$lt;inf$gt;2$lt;/inf$gt;O$lt;inf$gt;3$lt;/inf$gt; Red Phosphor Monospheres: Size-controlled Processing and Luminescence Property

Two-steps Prepared Monodisperse Li-doped Y2O3:Eu3+ Microspheres and Their Luminescence Properties

Synthesis and Properties of Europium-Based Phosphors on the Nanometer Scale: Eu2O3, Gd2O3:Eu, and Y2O3:Eu.

Luminescent Properties of Y2O3:Eu Synthesized by Sol–gel Processing

Electron capture dissociation of b (2+) peptide fragments reveals the presence of the acylium ion structure.

Facile Synthesis and Luminescence Properties of Uniform and Well-Dispersed Yf3:Eu3+ Architectures

A Garnet-Based Ca2YZr2Al3O12:Eu3+ Red-Emitting Phosphor for N-Uv Light Emitting Diodes and Field Emission Displays: Electronic Structure and Luminescence Properties

Synthesis of Nanometer Y2o3 : Eu Phosphor and Its Luminescence Property

Electro-deposition of Y2O3:Eu3+ thin film phosphor and its luminescent properties

Solution Combustion Synthesis and Enhanced Luminescence of Eu3+-activated Y2Ce2O7 Phosphor Nanopowders

Preparation and Properties of Ti, Euco-Doped Y2o2s : 0.06ti, 0.08eu Phosphor with Red Long Afterglow

Synthesis and Luminescence Properties of New Red-Emitting Phosphors YGe0.5M0.5O4:Eu3+ (m=mo, W)

Synthesis of red-luminescent Eu3+-doped lanthanides compounds hollow spheres

Eu 2+ Stabilized at Octahedrally Coordinated Ln 3+ Site Enabling Red Emission in Sr 3 LnAl 2 O 7.5 (Ln = Y or Lu) Phosphors

Synthesis and Characterization of Monodispersed BaSO4/Y2O3:Eu3+ Core–shell Submicrospheres

Luminescence Properties of Eu 3+ -Doped New Scheelite-Type Compounds

BDNF genetic variations increase the risk of Alzheimer's disease-related depression.

Giant Red‐Shifted Emission in (Sr,Ba)Y 2 O 4 :Eu 2+ Phosphor Toward Broadband Near‐Infrared Luminescence

Afterglow and energy transfer from Ti to Eu3+ in Y2O2S : 0.03Eu,0.03Ti phosphor

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Synthesis and luminescence properties of Y 2O 3:Eu with flower-like microstructure