Abstract:Nano-scale nickel oxide materials were prepared by solvothermal method using nickel acetylacetonate, oleic acid and oleylamine as raw materials, octadecene as solvent and polyvinylpyrrolidone as surfactant. The effects of the ratio of reactants ratio, insulation time, surfactant and the mass of oleylamine on the microstructure, particle size, morphology, optics and catalytic properties of the product were investigated by X-ray diffraction (XRD), transmission electron microscope (TEM), ultraviolet-visible spectroscopy (UV-Vis) spectral analysis, and Tafel test. The specific experimental operations were: the oleic acid (OA) and 1-octadecene (ODE) was added into four flasks (500 mL) with heating and stirring. Nickel acetylacetonate was added when the temperature raise to 50 degrees C, then continuously stirring for 60 minutes at 120 degrees C before a certain amount of oleylamine (OAm) was added to the reaction system. The mixed solution was poured into the inner liner of the high temperature reactor. The reactor was covered and transferred to the electro-thermostatic blast oven for a period of time and then cooled to room temperature. The main research results were obtained: (1) The boundary of the original particles became smoothed after sintering, and the spherical particles become flake-shaped which might be attributed to the residual organic covering so the size of nickel oxide nanoparticles changed from the original 40 similar to 45 nm to 30 similar to 40 nm. (2) With the addition of PVP, the content of NiO phase increased and the particle size was controlled within 40 similar to 45 nm. The UV-Vis test showed that NiO belonged to direct band gap and the band gap width was 3.5 similar to 3.7 eV. (3) The Tafel analysis showed that the best catalytic activity with exchange current density J(0) was 1.23x10(-2) mA,cm(-2), where pure NiO could be obtained when the reactant ratio of n[Ni(acac)(2)] : n(OA)-1: 2, the additive PVP mass fraction was of 1.66%, the amount of oleylamine was of 30 mmol, and the temperature was of 200 degrees C for 8 h.

Preparation of Submicro-porous Nickel Wafers by Molding-Decomposition-Sintering Method Using Nickel Oxalate Nano-Rods As Precursors

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

Preparation of Fibrous Nickel Oxide Particles

Preparation of Nickel Porous Materials by Sintering Nickel Oxalate and Sodium Chloride after Blending and Reduction

Preparation and characterization of fibrous NiO particles by thermal decomposition of nickelous complex precursors

Investigation on Preparation of Nanoporous Arrays of NiAl-W

Preparation and characterization of NiO nanorods by thermal decomposition of NiC2O4 precursor

Preparation of fibrious nickel oxide particles by the method of chemical precipitation and pyrolysis

Preparation and corresponding structure of nickel foam

Solvothermal Preparation and Characterization of Nano-nickel Oxide

Precursor Synthesis of Fibrillar Nanocrystalline Nickel Powder

Preparation of Nanocrystalline NiO by Electrochemical Dissolution of Nickel

Shape-controlled Synthesis of Novel Precursor for Preparing Fiber-like Nickel Oxide Powders

Structure Micro- and Nanomodification by Cyclic Oxidation-Reduction Treatment of Porous Nickel Sintered Using a Space Holder

Preparation and Characterization of Nanometer Nickel

RESEARCH ON PREPARATION OF NICKEL POWDER BY ELECTROLYTIC DEOXIDATION FROM NiO

The preparation of nickel nanorods in water-in-oil microemulsion

The Synthesis of Novel NiO Microsphere Architectures with Electrochemical Behavior

Guidance Evolution Mechanism of Nickel Oxalate Micro-structure for Formation of Polycrystalline Nickel Nano-fibers

Spherical and Radiate Ni Particles Prepared by the Tartrate Precipitation and Thermal Decomposition Method

Synthesis of NiO nanorods by a novel simple precursor thermal decomposition approach