Abstract:Concrete is a multiphase composite material consisting of aggregates, mortar, and initial defects. This work aims to quantitatively study the distribution and evolution of initial defects under elevated temperatures. To minimize the effect of hydration process and thermal and endogenous shrinkage, concrete samples cured in water for 12 months is tested. In order to study the effect of external load on the initial distribution of defects within concrete, concrete samples without pre-loading and pre-applied with 30% of the failure load are selected as research objects. The evolution of defects within the concrete samples are characterized using scanning electron microscopy (SEM). By employing an image processing software, the two-dimensional configurations of defects are extracted from the backscattered images obtained by SEM. Each defect is identified and approximated using an optimal ellipse. Thereafter, the defects are automatically recognized and classified into microcracks and pores by utilizing the image processing software and MATLAB programming. Consequently, the distribution and propagation of microcracks and pores in concrete could be quantitatively and separately analyzed. Statistical analysis of area, perimeter, and fitting ellipse parameters (e.g., major axis, minor axis, coordinates of the center, axis orientation, aspect ratio, and solidity) can provide the distribution of initial defects within concrete. It is demonstrated that the area of microcracks consistently increases with temperature. Log-normal and normal distributions may be suitable for the distribution of aspect ratio and solidity of microcracks, respectively, for both concrete samples with and without pre-applied loading under all elevated temperatures (40, 105, 150, 200, and 250 celcius). However, the distributions of area, coordinates of the center, and axis orientation of microcracks may vary with the initial concrete loading condition and temperature. For the pre-loaded concrete sample, the distribution of parameters does not conform to any type of distributions. Moreover, for the sample without pre-loading, the distributions of area, coordinates of the center, and axis orientation of microcracks exhibit good fitting precisions with log-normal, normal, and normal distributions, respectively at lower temperatures (40-150 celcius); however, such relationships do not apply at higher temperatures (200 and 250 celcius). As reference for identifying the variations in microstructures, 150 celcius is selected as the threshold temperature. The statistical approach employed in this study can lay the theoretical and experimental bases for determining the microstructure evolution in concrete. It can also be used for identifying the meso-defect and macro-defect and establishing their relationship with concrete properties. (c) 2021 Elsevier Ltd. All rights reserved.

Failure Mechanism Criterion for Multiaxial Strength of Concrete after Exposure to Normal and High Temperatures

A Micromechanical-Based Failure Criterion for Rocks after High-Temperature Treatment

Distortion Strain Energy–Based Mohr-Coulomb Criterion for Concrete Failure

Unified Failure Criteria for Freeze-Thaw Damaged Concrete under Multiaxial Stress State: an Innovative Uniaxial Strength-Dependent Prediction Method

An Improved Failure Criterion for the Concrete Based on Unified Twin Shear Strength Theory

Concrete Failure Criterion under Freeze-Thaw Condition in Structural Engineering

Investigating High-Temperature Deformation Evolution of Concrete under Sustained Loading Using DIC Technology and a Temperature-Mechanical Coupled Damage Constitutive Model

Restrained Cracking Failure Behavior of Concrete Due to Temperature and Shrinkage

Concrete Thermal Failure Criteria, Test Method, and Mechanism: A Review

A novel three-dimensional modified Griffith failure criterion for concrete

Statistical Analysis of Defects Within Concrete under Elevated Temperatures Based on SEM Image

Evaluation of several multiaxial failure criteria for concrete after freeze-thaw (F-T) cycles

Statistical Reliability Analysis of Ultrasonic Velocity Method for Predicting Residual Strength of High-Strength Concrete under High-Temperature Conditions

Experimental Study on the Compressive Strength and Fatigue Life of Cement Concrete under Temperature Differential Cycling

Effect of High Temperature on Residual Mechanical Properties of Confined and Unconfined High-Strength Concrete

Comparison between high strength concrete and normal strength concrete subjected to high temperature

Residual Compressive Strength of High-Strength Concrete Exposed to Elevated Temperatures

Study on the Constitutive Relationship between Ordinary Concrete and Nano-Titanium Dioxide-Modified Concrete at High Temperature

Failure criterion for concrete under volumetric stress state conditions

Static-Dynamic Combined Multiaxial Strength Criterion For Concrete

Experimental Investigation of the Static Expansion Tensile Behavior of Concrete after Exposure to Elevated Temperatures