Abstract:In this paper, a novel hard nickel composite coatings were fabricated by wide-band laser cladding technique. The effects of Si alloying on the composite coatings were investigated by microstructure characterization, phase identification, microhardness and wear resistance. Results showed that the in-situ precipitated phases in the laser molten pool were composed of the γ-Ni solid solution and hard phases such as Cr 23 C 6 , CrSi, Cr 5 B 3 . With the increase of Si element, the morphology of the precipitated phases changed significantly. When the added content of Si was 1.0 wt.%, the precipitated phase was a mainly block morphology. As the added content of Si was increased to more than 2.0 wt.%, the main precipitated phase was transformed into a long stripe morphology. With the increase of Si content, the stripe-like precipitated phase was gradually refined and finally becomes density needle-like precipitates. Element distribution analysis showed that the block precipitated phase was enriched in Cr, W and Si elements. Additionally, the enriched elements in the long strip precipitation phase were essentially the same as those in the block precipitation phase. The added Si element was highly involved in the in-situ reactions of precipitated phase. The TEM results showed that the precipitated phases contained the crystal structures of Cr 5 B 3 and Cr 7 C 3 . The pin-on-disc wear tests revealed that the composite coating with the addition of 6 wt.% Si exhibited the best wear resistance in the experimental group. The average friction coefficient was about 0.6 and the wear mass loss rate was about 2.38 × 10 −5 g/m under counter-abrasive conditions. The worn surface analysis indicated that the wear mechanism of composite coatings was mainly abrasive wear. The refined needle-like precipitated phase was closely bound to the matrix and thus not easy to peel off, providing a significant improvement in the wear resistance of the laser cladding coatings.

The Influence of Pulse Plating Parameters on Microstructure and Properties of Ni-W-Si3N4 Nanocomposite Coatings

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

The Influence of Pulse Plating Parameters on the Structure and Corrosion Behavior of Ni-W-TiC Nanocomposite Coatings

Influence of Electrodeposition Process Parameters and Si3N4 Nanoparticle Concentration on Microhardness and Wettability of Ni-Co-Si3N4 Nanocomposite Coatings

Process and Micromorphology of Ni-SiC Nano Composite Coating by Pulse Plating

Effect of SiC Nanoparticles on the Structure and Properties of Ni+W-SiC Nanocoatings

Preparation and Characterization of Pulse Electrodeposited Ni/W-SiC Nanocomposite Coating on Mild Steel Substrate

Preparation, Mechanical Properties and Wear Resistance of Ni–W/SiC Nanocomposite Coatings

Fabrication and Performance of Ni-Co-P/Si<sub>3</sub>N<sub>4</sub> Electroplated Composite Coatings on Al-Si Alloys

A Study on the Electrocodeposition Processes and Properties of Ni–SiC Nanocomposite Coatings

Impact of SiC Sizes on the Structure and Characteristics of Pulse Electrodeposited Ni/W-SiC Nanocomposites

Enhanced mechanical and wear properties of Ni-W-SiC composite coatings by synergistic influence of micro-nano SiC mixture

Effect of Nano-Sic Particles on the Corrosion Resistance of NiP-SiC Composite Coatings

Synthesis and Evaluation of Pulse Current and Direct Current Electroplating Ni-W Coatings on Steel

Impact of ultrasonic power density on the structure and performance of Ni-W-SiC composite nanocoatings

Effect of Pulse Electrodeposition Mode on Microstructures and Properties of Ni-TiN Composite Coatings

Investigation on the Microstructure Evolution and Properties of a Novel In-Situ Fiber Phase-Reinforced Nickel Composite Coating Deposited by Wide-Band Laser

Investigation on Microstructure and Properties of the Electrodeposited Ni-SiC Composite Coating

CORROSION BEHAVIOR OF THE Ni-SiC NANOCOMPOSITE COATINGS

Electrochemical Behavior of Electroless Ni-P-SiC Nano-Composite Coatings

Comparative study on the wear resistance and corrosion resistance of NiW and NiCoW composite coatings with micro- and nano-SiC particles