Abstract:Highly stable hierarchical ZSM-5 zeolites with intra-crystalline mesopores and inter-crystalline macropores have been synthesized via a steam-assisted conversion in the presence of polyethylene glycol. XRD, SEM, TEM, N-2 sorption and mercury intrusion measurement revealed that the irregular intra-crystal mesopores (2-10 nm) in each zeolite nanocrystal were generated by the removal of encapsulated PEG, and the inter-crystalline macropores (50-90 nm) were formed by the aggregation of the well crystallized ZSM-5 nanocrystals with a small size (50-200 nm). The ZSM-5 zeolite nanocrystals were achieved by a dense-gel with high TPA(+)/SiO2, highly concentrated TPA(+) can induce a burst in nucleation rate during the first step of steam-assisted conversion, which makes the dry gel easy to convert into zeolite nanocrystals, PEG arrested in the gel can be easily encapsulated by zeolite crystals during the steam-assisted conversion. Finally, these nanocrystals containing intra-crystalline mesopores aggregate into the bulky materials with an inter-crystalline macroporous network. In addition, the mesopore volume and external surface areas of Hier-ZSM-5 can be easily adjusted by changing the amount of PEG. Catalytic tests showed that Hier-ZSM-5 had a similar activity to Nano-ZSM-5, which must be collected by high-speed centrifugation; while had a higher activity than Con-ZSM-5, especially for the reactions involving large molecules. The high catalytic activity and easy separation from liquid mixture of Hier-ZSM-5 would facilitate its practical applications in chemical industry. Crown Copyright (c) 2013 Published by Elsevier B.V. All rights reserved.

Hollow Zsm-5 Zeolite Microspheres with Improved Adsorption and Catalytic Properties

ZSM-5 Zeolite Single Crystals with B-Axis-aligned Mesoporous Channels As an Efficient Catalyst for Conversion of Bulky Organic Molecules.

High-Surface-Area Zeolitic Silica with Mesoporosity

Hierarchical Shell-Like ZSM-5 with Tunable Porosity Synthesized by Using a Dissolution-Recrystallization Approach.

Facile synthesis of hollow zeolite microspheres through dissolution-recrystallization procedure in the presence of organosilanes

Hierarchically Tetramodal-Porous Zeolite ZSM-5 Monoliths with Template-Free-derived Intracrystalline Mesopores

Synthesis and Characterization of Hollow Zeolite Microspheres with a Mesoporous Shell by O/W/O Emulsion and Vapor-Phase Transport Method

Highly Stable Hierarchical ZSM-5 Zeolite with Intra- and Inter-Crystalline Porous Structures

Facile Morphology and Porosity Regulation of Zeolite ZSM-5 Mesocrystals with Synergistically Enhanced Catalytic Activity and Shape Selectivity

Zeolite Microspheres with Hierarchical Structures: Formation, Mechanism and Catalytic Performance

Synthesis and excellent catalytic properties of hierarchical ZSM-5 zeolite by organosilanized doubleterminal amino polyetheramine template method

Defective sites in ZSM-5 zeolite synthesized by n-butylamine template facilitating uniform meso-microporosity by alkali-treatment

Synthesis and catalytic activity of stable hollow ZrO2–SiO2 spheres with mesopores in the shell wall

Shape-controlled Synthesis of Monolithic ZSM-5 Zeolite with Hierarchical Structure and Mechanical Stability

Facile synthesis of hierarchical porous ZSM-5 zeolite with tunable mesostructure and its application in catalytic cracking of LDPE

Facile synthesis of hierarchical macro/microporous ZSM-5 zeolite with high catalytic stability in methanol to olefins

Spherical Binderless 4A/5A Zeolite Assemblies: Synthesis, Characterization, and Adsorbent Applications

Tuning Hierarchical ZSM-5 Zeolite for Both Gas- and Liquid-Phase Biorefining

Synthesis of hollow mesoporous aluminosilicate spheres and its catalytic cracking properties

Synthesis of Zsm-5 Aggregates Made of Zeolite Nanocrystals Through A Simple Solvent-Free Method

Synthesis of hollow HZSM-5 zeolite-based catalysts and catalytic performance in MTA reaction