Novel cross-linked membrane for direct methanol fuel cell application: sulfonated poly(ether ether nitrile)s

Penglun Zheng,Mingzhen Xu,Xiaobo Liu,Kun Jia

DOI: https://doi.org/10.1007/s11581-016-1805-z

IF: 2.961

2016-01-01

Ionics

Abstract:In order to reduce water uptake, swelling ratio, and methanol permeability in sulfonated proton exchange membranes (PEM), novel-sulfonated aromatic poly(ether ether nitrile)s-bearing pendant propenyl groups had been synthesized by direct copolymerization method. All the results showed that the propenyl groups were suitable cross-linkable groups, and that this method was an effective way to overcome the drawbacks of sulfonated polymers at high ion exchange capacity (IEC) values. By cross-linking, the water uptake, swelling ratio, and methanol diffusion could be restricted owing to the formation of compact network structure. For example, CSPEN-60 membranes showed the proton conductivity of 0.072 S cm −1 at 80 °C, while the swelling ratios and water uptake (17.9 and 60.7 %) were much lower than that of the SPEN-60 membrane (60.8 and 295.2 %). Meanwhile, a 1.1 × 10 −7 cm 2 s −1 of methanol diffusion was obtained which was much lower than that of Nafion 117 (14.1 × 10 −7 cm 2 s −1 ). Although the proton conductivity of the CSPEN-60 membranes is lower than that of the SPEN-60 membrane, the selectivity is much higher. The CSPEN-60 membrane exhibited the highest selectivity among the tested membranes, about 5.8 times higher compared with that of Nafion117.