Structural and Electrical Properties of Bi1/2Na1/2TiO3–BaTiO3–Sr3CuNb2O9 Lead-Free Piezoelectric Ceramics

Hao Zhang,De-yi Zheng,Shun-min Hu,Cheng,Gui-gui Peng,Jing Zhang,Liang-liang Li

DOI: https://doi.org/10.1007/s10854-016-5493-2

2016-01-01

Journal of Materials Science Materials in Electronics

Abstract:The structure, microstructure, field-induced strain, ferroelectric, piezoelectric and dielectric properties of (1 - x) (Bi0.5Na0.5)(0.935)Ba0.065TiO3-xSr(3)CuNb(2)O(9) (BNT-BT6.5-xSCN, with x = 0, 0.003, 0.006, 0.009) ceramics were investigated. X-ray diffraction patterns show that all samples are pure perovskite structure and Sr3CuNb2O9 (SCN) effectively diffused into the 0.935Bi(0.5)Na(0.5)TiO(3)-0.065BaTiO(3) (BNT-BT6.5) solid solution which also reflected in the Raman spectra and the energy disperse spectroscopy (EDS) analysis. With the increases of SCN content, the coercive field (E-c = 18.41 kV/cm) decreases greatly, whereas the remnant polarization (P-r = 29.11 mu C/cm(2)) increases a little at x = 0.003 which is showed in the polarization hysteresis (P-E) loops, the result indicate that the ferroelectric order would be disrupted. Around critical composition (x = 0.003) at a driving field of 60 kV/cm, a large unipolar strain of 0.29 % with a normalized strain (d(33)* = 483 pm/V) is obtained at room temperature. The results indicate that BNT-BT6.5-xSCN ceramics with excellent properties are promising to replace lead-based piezoelectric ceramics and can be used in practical applications.