Rare earth induced lattice distortion of Bi 2 WO 6 to effectively improve photocatalytic performance: experimental and DFT calculations
Morigejile Liu,Morigen Bao,Hongzhang Cao,Xiaoli Yu,Si Qin Zhao
DOI: https://doi.org/10.1016/j.optmat.2024.115798
IF: 3.754
2024-07-14
Optical Materials
Abstract:The excellent visible light photocatalytic activity of bismuth-based photocatalysts has attracted the interest of many scholars at home and abroad. In this paper, rare earth (Sm, La, Ce, Eu) doped Bi 2 WO 6 photocatalysts were prepared by a one-step hydrothermal method using bismuth nitrate and sodium tungstate as precursors. The microstructures and spectroscopic performances of prepared materials were investigated utilizing characterization methods, such as XRD, XPS, UV-vis, TEM, and N 2 adsorption-desorption, etc., and the effluent removal performances were studied by using rhodamine B as a simulated degradation dye and the photodegradation mechanism was investigated in combination with DFT calculations. XRD indicates that the rare earth doping leads to the lattice distortion of the (131) crystal surface of Bi 2 WO 6, and the relative amount of distortion is directly proportional to the photocatalytic activity; UV-vis spectra show that the absorption edge of Bi 2 WO 6 is obviously red-shifted with the rare earth doping, and N 2 adsorption-desorption curve show that the doped rare earths make the specific surface area of the sample effectively increased. Moreover, XPS spectrum suggest that the doped rare earth Ce and Eu often exist in the form of metastable oxidation states, and the transformation between Ce 3+ /Ce 4+ and Eu 2+ /Eu 3+ oxidation states is easy to form impurity energy levels between Bi 2 WO 6 , which make the energy level significantly enriched to broaden the absorption range and reduce band gap width of the material. DFT calculations further indicate that the rare earths successfully replace Bi sites. One of the main reasons for the improvement of photocatalytic activity is that rare earth doping is easier to replace Bi sites, leading to increased relative aberration; another one is that the arrangement of E VB and E CB in the photocatalytic mechanism is type-II, which contributes to red-shift of absorption edge and effective separation of electron-hole pairs in the photocatalytic process, thus improving the photocatalytic activity.
materials science, multidisciplinary,optics