Abstract:Ultrasonic damage detection and characterization is commonly used in nondestructive evaluation (NDE) of aerospace composite components. However, in real materials and structures, the dispersive waves can result in complicated behavior, particularly in the presence of complex damage scenarios and structural components. Accurate three dimensional finite element models (FEMs), using PZFlex, of guided wave interactions with realistic damage scenarios can be used to study quantitative NDE ultrasonic damage detection techniques numerically, to supplement or replace expensive experimental testing. Novel data analysis techniques such as filter reconstruction imaging methods can be used to create practical comparisons between experimental and simulated data. To compare experimental and simulated data, however, the FEM must accurately simulate the physics of an ultrasonic inspection. This requires that information about the damage be known a priori (e.g. through CT scans of the laminates). While possible in a research setting, this is typically not the case for real inspections in which the goal is to characterize the unknown damage. This work will describe a means of parameterizing a FEM of a composite laminate for use in a damage characterization scheme. The FEM is parameterized with a multidimensional damage model capable of describing the complex amage typical of low impact strikes in composites. The damage under consideration in this work is described by the spiraling, multilayer delamination depicted in Figure 1. Experimental laser Doppler vibrometer (LDV) wavefield data and the FEM simulated vibration responses are postprocessed using the 3D Fourier transform so that the wavenumber-frequency spectra can be readily compared, building on the results and methods in [1]. The purpose of the parameterized damage model is for use in a probabilistic damage characterization methodology, discussed in a companion presentation [2]. The composite laminate model and the ultrasonic inspection are simulated using PZFlex and allows for iterative refinement of the damage. The increasing model fidelity enables fast localization of the damage followed by subsequent refined characterization.

Ultrasonic Attenuation and Velocity Changes in Multilayer Structures Containing Multiple Delaminations

Identifying Delamination in Carbon Fiber Composites Based on Defect Modes in Imperfect Phononic Crystals

Delamination Analysis of Carbon Fiber/Epoxy Composite Laminates under Different Loading Rates Using Acoustic Emission

Guided wave energy trapping to detect hidden multilayer delamination damage

Static and dynamic diffuse wave inspection of delaminations in carbon fiber reinforced composites

Detection of Delamination using Laser-generated Lamb waves with Improved Wavenumber Analysis

Ultrasonic Phased Array Imaging Approach Using Omni-Directional Velocity Correction for Quantitative Evaluation of Delamination in Composite Structure

Delamination Detection in Composite Plates Using Linear and Nonlinear Ultrasonic Guided Waves

Influence of a delamination on Lamb wave excitation by a nearby piezoelectric transducer

Numerical Simulation of Carbon Fiber Reinforced Polymer Composite Delamination Damage Identification Using Lamb Wave and Filtered Back-Projection Method

A Parameterized Delamination Model for Use in Complex Damage Characterization of Composite Laminatesin Ultrasonic Inspections

Vibration-Based In-Situ Detection and Quantification of Delamination in Composite Plates

Delamination assessment of a laminated composite beam using distributed piezoelectric sensor/actuator

Detection of Multi-Layered Bond Delamination Defects Based on Full Waveform Inversion

Prediction of delamination growth in laminated composites using acoustic emission and Cohesive Zone Modeling techniques

Effect of delamination on the dynamic characteristics of thin‐walled carbon fiber‐reinforced polymer tube

Finite Element Model for Adhesive Force of Multilayer Ceramic Capacitors and Failure Analysis

Delamination detection in laminated composite beams using electro-mechanical impedance signatures

Damage Localization, Identification and Evolution Studies during Quasi-Static Indentation of CFRP Composite Using Acoustic Emission

Phase-Field Modeling of Electromechanical Breakdown in Multilayer Ceramic Capacitors

Numerical simulation of Lamb wave sensing of low-velocity impact damage in composite laminate