Structural chemistry and magnetic properties of Y{sub 2}CoGe{sub 4}O{sub 12}

Xiao-Qiang Liu,Joe Ridout,Diming Xu

DOI: https://doi.org/10.1016/J.JSSC.2015.04.033

IF: 3.3

2015-01-01

Journal of Solid State Chemistry

Abstract:Polycrystalline Y{sub 2}CoGe{sub 4}O{sub 12} has been prepared by standard ceramic methods. The crystal structure (space group P4/nbm; a=9.8465(2), c=4.92986(9) A) consists of metal-rich layers separated from each other by Ge{sub 4}O{sub 12} groups comprised of four corner-sharing GeO{sub 4} tetrahedra. Two cation sites lie within the layers; an eight-coordinate site occupied by yttrium and a six-coordinate site occupied by a 1:1 disordered distribution of yttrium and cobalt. Neutron diffraction revealed two-fold disorder on the oxide sublattice; this has been elucidated using Co K-edge EXAFS spectroscopy. The availability of two sites allows each oxide ion to accommodate the coordination preferences of its single Co/Y neighbour; the GeO{sub 4} tetrahedra distort to absorb any consequent strain. The octahedron of anions around each Co{sup 2+} cation shows a pseudo-tetragonal distortion with a strain (Co–O){sub eq}–(Co–O){sub ax}/(Co–O){sub eq}=−0.173. This results in an unusually large effective magnetic moment of 6.05 µ{sub B} per Co{sup 2+} cation. - Graphical abstract: A distorted coordination environment leads to an unusually large effective magnetic moment of Co{sup 2+} in Y{sub 2}CoGe{sub 4}O{sub 12}. - Highlights: • Co{sup 2+} and Y{sup 3+} occupy the same site in a disordered manner. • Distorted coordination geometry around Co{sup 2+} results inmore » an unusually large effective magnetic moment. • Use of neutron diffraction and EXAFS to probe average structure and local structure, respectively.« less