Abstract:Si-modified NiAl coating has been studied by researchers due to its good performance in high temperature corrosive environment, but the effect of Si content on the high temperature oxidation resistance of the aluminide coatings has been seldom studied. To figure out this issue, three modified NiAl coatings with different Si contents were prepared by varying the Si contents 8wt%, 17wt% and 30 wt% in the slurry. Phase structures and microstructures of the simple NiAl coatings and three Si-modified NiAl coatings before and after oxidation were analyzed by XRD, SEM and EPMA, etc. The results show that the delta-Ni2Al3 and ss-NiAl are the primary phases of the four aluminide coatings. Si mainly locates in the upper zone of the Si-modified NiAl coatings in the form of silicides as CrSi2, Cr5Si3 and Ni2Si. After oxidation at 1000. for 500 h, the simple NiAl coating has the maximum mass gain of 1.93 mg/cm(2), while the Si-modified NiAl coating with Si content of 8wt% has the smallest mass gain. The dopant of Si into NiAl coatings can promote the formation of protective alpha-Al2O3 film, retard the outward diffusion of refractory metal elements and improve the surface quality of the oxide film, resulting in reduced oxidation rate. However, the addition of Si reduces the Al content on the surface layer of the coating and may make the coating insufficient of ss phase to maintain the selective oxidation of Al in the later period of long- time oxidation. Therefore, when the Si content is 8wt%, the Si-modified NiAl coating possesses the best oxidation resistance.

Oxidation Behaviour of the Nickel-Based Superalloy Dz125 Hot-Dipped with Al Coatings Doped by Si

High Temperature Oxidation Resistance and Degradation Mechanism of Al-Si Coatings on Nickel-Based Superalloy at 1000.

The Effects of Alloying Elements Cr, Al, and Si on Oxidation Behaviors of Ni-Based Superalloys

Effect of Ni in SiO 2 coating on the oxidation resistance of TiAl alloy at 900 °C

Investigation of the Role of Silicon in TiAlSiN Coating Deposited on TiAl Alloys during Long-term Oxidation

Cyclic Oxidation Behaviour of Pt-doped Aluminide Coating on DZ125 Containing Hf

Structure and High-Temperature Oxidation Performance of Si-Co Diffusion Coatings Prepared on a TiAl-Nb Alloy

The oxidation behavior and interfacial reaction between SiO 2 coating and Ti45Al8.5Nb alloy

Cyclic oxidation behavior of Al-Si coating on new γ′-strengthened cobalt-based superalloy: Experimental study and first-principles calculation

Improving oxidation resistance of γ-TiAl based alloy by depositing TiAlSiN coating: Effects of silicon

Effect of Pre-Oxidation on High-Temperature Oxidation Behavior of Al-Si Coating on Nickel-Based Superalloy

Research on high-temperature oxidation resistance, hot forming ability, and microstructure of Al–Si–Cu coating for 22MnB5 steel

Improving the high temperature oxidation resistance of TiAl alloy by SiOC coating

High temperature oxidation behavior of TiAl alloy with electrodeposited SiOC coating

Microstructure and hot corrosion behavior of Al-Ce-Y coatings on DZ125 nickel-based alloy prepared by pack cementation process

Effects of Annealing and Oxidation on the Microstructure of Hot-Dipped Aluminum–Silicon Coating of 316L Stainless Steel

Cyclic Oxidation Behavior of the Aluminide Coatings on the Co-Base Superalloy DZ40M

Effect of Nickel Aluminide Microcrystalline Coating on High-Temperature Oxidation Behavior of NiAl-33.5%Cr-0.5%Zr Alloy

Oxidation behavior of AlCoCrFeNiSi high-entropy alloys at 1100 °C

High-temperature oxidation behavior of aluminide coatings on a new cobalt-base superalloy in air

High Temperature Oxidation and Wear Resistance of Y-Modified Hot Dipping Aluminized Coating on Sch12 Steel