Anchoring Mo single atoms on N-CNTs synchronizes hydrogenation/dehydrogenation property of Mg/MgH 2
Congwen Duan,Yating Tian,Xinya Wang,Jinhui Wu,Bogu Liu,Dong Fu,Yuling Zhang,Wei Lv,Lianxi Hu,Fei Wang,Xu Zhang,Ying Wu
DOI: https://doi.org/10.1016/j.nanoen.2023.108536
IF: 17.6
2023-05-19
Nano Energy
Abstract:MgH2 has attracted substantial consideration mainly due to its sufficient content and high gravimetric density etc. However, its high thermodynamic stability and poor dynamics hinder its practical application. N-doping carbon nanotubes (N-CNTs) supported Mo single atoms (MoSA-N-CNTs) was constructed to facilitate the hydrogenation/dehydrogenation properties of the Mg/MgH 2 system. According to the synergistic effect of N-CNTs nanoconfinement and MoSA catalysts, can absorb 7.37 wt.% H 2 during the milling within 15 h and the corresponding activation energy for hydrogenation can be reduced to 21.2 kJ·mol -1 . releases 7.23 wt% H2 at 325 °C for 5 min, nearly 3 times pristine MgH2. Meanwhile, its initial dehydriding temperature decreases from 265.7 to 204.6°C, and its apparent activation energy for dehydrogenation also greatly decreases from 108.6 kJ/mol to 68.4 kJ/mol. The above values are much lower than the pure MgH2. The synergistic effect mechanism of N-CNTs and MoSA on hydrogenation/dehydrogenation properties of Mg/MgH 2 is proposed systemically. It is revealed that the MoSA and the N-CNTs not only accelerate H 2 dissociation and diffusion but also effectively prevent the Mg/MgH 2 nanoparticles agglomeration. The above results highlight the great promise of Mg/MgH 2 @MoSA-N-CNTs composite for high-performance Mg-based hydrogen storage materials.
materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology