Abstract:Two-dimensional vanadium carbide (V2C) and titanium carbide (Ti3C2) MXenes were first synthesized by exfoliating V2AlC or Ti3AlC2 and then introduced jointly into magnesium hydride (MgH2) to tailor the hydrogen desorption/absorption performances of MgH2. The as-prepared MgH2-V2C-Ti3C2 composites show much better hydrogen storage performances than pure MgH2. MgH2 with addition of 10 wt % of 2V(2)C/Ti3C2 initiates hydrogen desorption at around 180 degrees C; 5.1 wt % of hydrogen was desorbed within 60 min at 225 degrees C, while 5.8 wt % was desorbed within 2 min at 300 degrees C. Under 6 MPa H-2, the dehydrided MgH2-2V(2)C/Ti3C2 can start to recover hydrogen at room temperature, and 5.1 wt % of H-2 is obtained within 20 s at a constant temperature of 40 degrees C. The reversible capacity (6.3 wt %) does not decline for up to 10 cycles, which shows excellent cycling stability. The addition of 2V(2)C/Ti3C2 can remarkably lower the activation energy for the hydrogen desorption reaction of MgH2 by 37% and slightly reduce the hydrogen desorption reaction enthalpy by 2 kJ mol(-1) H-2. It was demonstrated that the combination of V2C and Ti3C2 promotes the hydrogen-releasing process of MgH2 compared with addition of only V2C or Ti3C2, while Ti3C2 impacts MgH2 more significantly than V2C in the hydrogen absorption process of MgH2 at ambient temperatures. A possible mechanism in the hydrogen release and uptake of the MgH2-V2C-Ti3C2 system was proposed as follows: hydrogen atoms or molecules may preferentially transfer through the MgH2/V2C/Ti3C2 triple-grain boundaries during the desorption process and through the Mg/ Ti3C2 interfaces during the absorption process. Microstructure studies indicated that V2C and Ti3C2 mainly act as efficient catalysts for MgH2. This work provides an insight into the hydrogen storage behaviors and mechanisms of MgH2 boosted by a combination of two MXenes.

Effects of Cnts on the Hydrogen Storage Properties of Mgh2 and Mgh2-Bcc Composite

Effects of Nano-Composites (feb, FeB/CNTs) on Hydrogen Storage Properties of MgH2

Enhanced Hydrogen Storage Properties of MgH2 by the Synergetic Catalysis of Zr0.4Ti0.6Co Nanosheets and Carbon Nanotubes

Hydrogen Storage Properties of Nano-Cob/cnts Catalyzed MgH2

The Dehydrogenation Mechanism and Cycling Property of MgH 2 Modified by CoB/CNTs Addition

Experimental and Theoretical Investigation on the Enhanced Hydrogen Storage Performance of Ti–Cr–Mn–Fe-Based Alloys Modified by Nb Substitution

Hydrogen Storage Properties Of Mg-Bcc Composite

CNTs Decorated with CoFeB As a Dopant to Remarkably Improve the Dehydrogenation/rehydrogenation Performance and Cyclic Stability of MgH2

Achieving superior hydrogen storage properties of MgH<sub>2</sub> by the effect of TiFe and carbon nanotubes

Carbon composite support improving catalytic effect of NbC nanoparticles on the low-temperature hydrogen storage performance of MgH2

The Effect of a Ti-V-based BCC Alloy As a Catalyst on the Hydrogen Storage Properties of MgH2

Combinations of V2C and Ti3C2 MXenes for Boosting the Hydrogen Storage Performances of MgH2

Novel 1D Carbon Nanotubes Uniformly Wrapped Nanoscale MgH2 for Efficient Hydrogen Storage Cycling Performances with Extreme High Gravimetric and Volumetric Capacities

Enhancing hydrogen storage capacity: MWCNT-infused Mg–Ti alloy synthesized via mechanical alloying

Highly-dispersed Nano-Tib2 Derived from the Two-Dimensional Ti3CN MXene for Tailoring the Kinetics and Reversibility of the Li-Mg-B-H Hydrogen Storage Material

Ti 3 AlCN MAX for tailoring MgH 2 hydrogen storage material: from performance to mechanism

Hybrid of Bulk NbC and Layered Nb4C3 MXene for Tailoring Hydrogen Storage Kinetics and Reversibility of Li-Mg-B-H Composite: an Experimental and Theoretical Study

Positive and Negative Effects of Carbon Nanotubes on the Hydrogen Sorption Kinetics of Magnesium

Hydrogen Storage Properties and Crystal Structure of Ti-Cr Based Alloys

Effect of Ti0.9Zr0.1Mn1.5V0.3 alloy catalyst on hydrogen storage kinetics and cycling stability of magnesium hydride

Hydrogen Storage Properties of Mg+10% TiFe_(1-x)Cr_x(x=0,0.3) Multi-Phase Alloys