Abstract:The integrity of delaminated composite structures can be restored by introducing a thermally-based healing effect on continuous fiber-reinforced thermoplastic composites (CFRTPC). The phenomenon of thermoplastics retaining their properties after melting and consolidation has been applied by heating the delaminated composite plates above their glass transition temperature under pressure. In the current investigation, the composite is comprised of Methyl methacrylate (MMA)-based infusible lamination resin combined with benzoyl peroxide initiator, which polymerizes into a Polymethyl methacrylate (PMMA) matrix. For the reinforcement, unidirectional 220 gr/m2 glass filament fabric was used. Delamination damage is artificially induced during the fabrication of laminate plates. The distributed delamination region before and after thermally activated healing was determined by using non-destructive testing with active thermography. An experimental approach is employed to characterize the thermal healing effect on mechanical properties. Experimentally determined technological parameters for thermal healing have been successfully applied to repair delamination defects on composite plates. Based on the compression-after-impact (CAI) test methodology, the intact, damaged, and healed composite laminates were loaded cyclically to evaluate the healing effect on stiffness and strength. During the CAI test, the 3D digital image correlation (DIC) technique was used to measure the displacement and deformation fields. Experimental results reveal the difference between the behavior of healed and damaged specimens. Additionally, the numerical models of intact, damaged, and healed composite laminates were developed using the finite element code LS-Dyna. Numerical models with calibrated material properties and tie-break contact constants provide good correlation with experimental results and allow for the prediction of the mechanical behavior of intact, damaged, and healed laminated plates. The comparison analysis based on CAI test results and modal characteristics obtained by the 3D Laser Doppler Vibrometer (Polytec GmbH, Karlsbad, Germany) proved that thermal healing partially restores the mechanical properties of damaged laminate plates. In contrast, active thermography does not necessarily indicate a healing effect.

Detection and Characterisation of Delamination Damage Propagation in Woven Glass Fibre Reinforced Polymer Composite Using Thermoelastic Response Mapping

Research on Internal Defect Detection of Epoxy Glass Fiber Composites Based on Terahertz Imaging Technology

Delamination Analysis of Carbon Fiber/Epoxy Composite Laminates under Different Loading Rates Using Acoustic Emission

J046033 Evaluation of Delamination in Fiber Reinforced Composites by Microwave Propagation Theory

An Experimental Analysis for Damage Monitoring in Glass Fiber/Epoxy Composites During Fatigue Tests by Acoustic Emission

Detection of Delamination in GFRP and CFRP by Microwaves with Focusing Mirror Sensor

3D photothermal reconstruction of subsurface defects in notched multidirectional CFRP laminates due to tensile fatigue loading

Cluster analysis of acoustic emission signals and infrared thermography for defect evolution analysis of glass/epoxy composites

Nondestructive Testing of Defects in Polymer–Matrix Composite Materials for Marine Applications Using Terahertz Waves

Delamination inspection in composite laminates with S0 Lamb wave using flexible macro-fiber composite transducers

Characterization of failure mechanism in glass, carbon and their hybrid composite laminates in epoxy resin by acoustic emission monitoring

Experimental study on delamination identification in tapered laminated composite plates using damage detection models

Full-field investigation of dissipative mechanisms and thermoelastic inversion effects within glass-fiber reinforced polyamides subjected to low-cycle fatigue

Interlaminar Fracture Toughness Evaluation in Glass/Epoxy Composites Using Acoustic Emission and Finite Element Methods

Structural health monitoring of carbon nanotube-modified glass fiber-reinforced polymer composites by electrical resistance measurements and digital image correlation

Predicting delamination of composite laminates using an imaging approach

High‐speed observation of dynamic delamination failure in tapered composite laminates under tensile loading

Diagnosis of early-stage damage to polymer - glass fibre composites using non-contact measurement of vibration signals

Experimental and Numerical Study of Healing Effect on Delamination Defect in Infusible Thermoplastic Composite Laminates

Application of Mechano-Luminescence-Optoelectronic Composites for Delamination Detection in Fiber Reinforced Polymer Composites

Investigation of self-heating and damage progression in woven carbon fibre composite materials, following the fibres direction, under static and cyclic loading